LNP™ ELCRIN™ WF006XiQ
PBT
沙特基础 (SABIC)
产品描述
LNP ELCRIN WF006XiQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 37% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. Added features of this grade include: Excellent Strength, Stiffness and Dimensional Stability. Potential applications may include handles, connectors.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性尺寸稳定填充增强含回收料 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.54 g/cm³ | ISO 1183 | |
密度 | 1.54 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
250°C/5.0 kg | 38 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
250°C/5.0 kg | 52 g/10 min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | 3.2mm |
横向(Across Flow) | 0.8~1 % | Internal | 3.2mm |
吸水率 | 0.1 % | ASTM D570 | 23°C/24hrs |
吸水率 | 0.09 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.1 % | ISO 62 | 23°C/50%RH |
回收料含量(PCR) | 37 % | Internal | Min. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 114 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 139 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 139 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 114 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 2.2 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 1.6 % | ISO 527 | 5 mm/min |
断裂(brk) | 2.2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 1.6 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 210 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 210 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 189 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 9100 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 9100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 11800 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 10700 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 14 kJ/m² | ISO 179/1eA | 80*10*4 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 83 J/m | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 82 J/m | ASTM D256 | |
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 770 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 7 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 203 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 207 °C | ASTM D648 | 6.4 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 25 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 89 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 89 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 200 °C | IEC 60695-10-2 | approximate maximum |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
绝缘强度 | 23 kV/mm | ASTM D149 | in air, 3.2 mm |