| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
比重 | 1.31 -
| ASTM D792 | |
比重 | 1.3 -
| ISO 1183 | |
熔体质量流动速率(MFR) | | | |
250°C/2.16 kg |
74 g/10min | ASTM D1238 | |
250°C/2.16 kg |
71 g/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
1.2~2.1 % | ASTM D 955 | 3.2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
54 Mpa | ASTM D638 | 50mm/min |
屈服(yld) |
55 Mpa | ISO 527 | 50mm/min |
断裂(brk) |
47 Mpa | ISO 527 | 50mm/min |
断裂(brk) |
46 Mpa | ASTM D638 | 50mm/min |
拉伸延伸率 | | | |
断裂(brk) |
4 % | ASTM D638 | 5mm/min |
断裂(brk) |
15 % | ISO 527 | 50mm/min |
弯曲强度 | | | |
- |
83 Mpa | ASTM D790 | 2.8mm/min |
- |
74 Mpa | ISO 178 | 2mm/min |
弯曲模量 | 2300 Mpa
| ASTM D790 | 2.8mm/min |
弯曲模量 | 2100 Mpa
| ISO 178 | 2mm/min |
拉伸模量 | 2200 Mpa
| ASTM D638 | 50mm/min |
拉伸模量 | 2300 Mpa
| ISO 527 | 50mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
4.9 kJ/m² | ISO 179/1eA | 4mm |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
27 J/m | ASTM D256 | 1/4 inch |
23℃ (73℉) |
28 J/m | ASTM D256 | 1/8 inch |
23℃ (73℉) |
4.5 kJ/m² | ISO 180/1A | 4mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 115 R
| ASTM D785 | |
洛氏硬度R | 117 R
| ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
170 °C | ASTM D648 | 6.4mm |
0.45 Mpa (66 psi)（4.6kg/cm²） |
124 °C | ISO 75-2 | Unannealed,4.0mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
75 °C | ASTM D648 | 6.4mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
59 °C | ISO 75-2 | Unannealed,4.0mm |
维卡软化温度(Vicat) | 185 °C
| ISO 306 | B/120 |
维卡软化温度(Vicat) | 188 °C
| ISO 306 | B/120 |
维卡软化温度(Vicat) | 188 °C
| ISO 306 | B/50 |
维卡软化温度(Vicat) | 194 °C
| ISO 306 | B/50 |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.7 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | | | |
1MHz |
3.1 - | IEC 60250 | |
1MHz |
3.1 - | ASTM D 150 | |
耗散因数(DF) | | | |
1MHz |
200 E-4 | IEC 60250 | |
1MHz |
200 E-4 | ASTM D150 | |
耐电弧性 | 140 sec
| ASTM D495 | |