LNP™ LUBRICOMP™ RL004S
PA66
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定耐磨 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 20% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ISO 1183 | |
密度 | 1.27 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.88~3.29 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 1.9~3.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1.9~3.3 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.88~3.29 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.55 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 63 Mpa | ASTM D638 | |
屈服(yld) | 55 Mpa | ISO 527 | |
断裂(brk) | 55 Mpa | ISO 527 | |
断裂(brk) | 63 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.4 % | ASTM D638 | |
屈服(yld) | 6.7 % | ISO 527 | |
断裂(brk) | 6.2 % | ASTM D638 | |
断裂(brk) | 7.2 % | ISO 527 | |
弯曲强度 | |||
- | 88 Mpa | ASTM D790 | |
- | 84 Mpa | ISO 178 | |
弯曲模量 | 2270 Mpa | ASTM D790 | |
弯曲模量 | 2400 Mpa | ISO 178 | |
拉伸模量 | 2480 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2600 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.32 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.21 - | ASTM D 3702 | Static COF |
磨损因数 | 16 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 42 J/m | ASTM D256 | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 571 J/m | ASTM D4812 | |
23℃ (73℉) | 39 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 3 J | ASTM D3763 | |
多轴冲击 | 0 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 97.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 79.2 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |