Zytel® FG42A NC010
Zytel® FG42A NC010
PA66
杜邦 (DuPont)
产品描述
Zytel® FG42A is a high viscosity polyamide 66 for injection molding and extrusion. It has improved break resistance for thick-walled parts. It has been developed for consideration into applications such as parts for the food industry.
FOOD CONTACT
Th
基本信息
| 原厂资料 | 物性表-ISO(中文) |
| 产品特性 | 食品接触级高粘度 |
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1140 kg/m³
| ISO 1183 | |
成型收缩率 | | | |
纵向(Flow) |
1.4 % | ISO 294-4, 2577 | |
横向(Across Flow) |
1.4 % | ISO 294-4, 2577 | |
吸水率 | 8.5 %
| ISO 62 | 2mm |
吸湿率 | 2.6 %
| ISO 62 | 2mm |
粘度 | 300 cm³/g
| ISO 307, 1157, 1628 | |
熔体密度 | 1010 kg/m³
| - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
83 Mpa | ISO 527-1/-2 | |
屈服(yld) |
55 Mpa | ISO 527-1/-2 | Conditioned |
拉伸延伸率 | | | |
屈服(yld) |
4.4 % | ISO 527-1/-2 | |
屈服(yld) |
27 % | ISO 527-1/-2 | Conditioned |
标称断裂伸长率 |
50 % | ISO 527-1/-2 | |
标称断裂伸长率 |
50 % | ISO 527-1/-2 | Conditioned |
弯曲模量 | 2800 Mpa
| ISO 178 | |
弯曲模量 | 1070 Mpa
| ISO 178 | Conditioned |
拉伸模量 | 3100 Mpa
| ISO 527-1/-2 | |
拉伸模量 | 1300 Mpa
| ISO 527-1/-2 | Conditioned |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
6 kJ/m² | ISO 179/1eA | |
-30℃ (-22℉) |
4 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) |
6 kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
20 kJ/m² | ISO 179/1eA | Conditioned |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Conditioned |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
7 kJ/m² | ISO 180/1A | |
-30℃ (-22℉) |
6 kJ/m² | ISO 180/1A | Conditioned |
23℃ (73℉) |
6 kJ/m² | ISO 180/1A | |
23℃ (73℉) |
23 kJ/m² | ISO 180/1A | Conditioned |
悬臂梁无缺口(Izod Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | Conditioned |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | Conditioned |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
200 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
70 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 244 °C
| ISO 306 | 50℃/h 50N |
相对温度指数(RTI) | | | |
冲击w/impact,0.75/0.8mm |
65 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm |
75 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm |
75 °C | UL 746B | |
冲击w/impact,6.0mm |
75 °C | UL 746B | |
电气Elec,0.75/0.8mm |
125 °C | UL 746B | |
电气Elec,1.5/1.6 mm |
125 °C | UL 746B | |
电气Elec,3.0/3.2 mm |
125 °C | UL 746B | |
电气Elec,6.0mm |
125 °C | UL 746B | |
强度w/o impact,0.75/0.8mm |
65 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm |
85 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm |
85 °C | UL 746B | |
强度w/o impact,6.0mm |
85 °C | UL 746B | |
比热容 | 2790 J/kg-K
| - | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
100 E-6/K | ISO 11359-1/-2 | |
横向(Across Flow) |
100 E-6/K | ISO 11359-1/-2 | |
熔融温度(Tm) | 262 °C
| ISO 11357-1/-3 | 10℃/min |
玻璃化温度(Tg) | 70 °C
| ISO 11357-1/-2 | 10℃/min |
导热系数 | 0.16 W/(m K)
| - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.5 mm | UL94 | |
V-2 |
3 mm | UL94 | |
氧指数(LOI) | 28 %
| ISO 4589-1/-2 | |
FMVSS | SE -
| FMVSS 302 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m
| IEC 60093 | |
体积电阻率 | 1.0E+11 Ohm-m
| IEC 60093 | Conditioned |
介电常数(DK) | | | |
100Hz |
4.3 - | IEC 60250 | |
100Hz |
10 - | IEC 60250 | Conditioned |
1MHz |
3.6 - | IEC 60250 | |
1MHz |
4.2 - | IEC 60250 | Conditioned |
耗散因数(DF) | | | |
100Hz |
150 E-4 | IEC 60250 | |
100Hz |
2000 E-4 | IEC 60250 | Conditioned |
1MHz |
150 E-4 | IEC 60250 | |
1MHz |
750 E-4 | IEC 60250 | Conditioned |
绝缘强度 | 31 kV/mm
| IEC 60243-1 | |