TECHNYL® MAX AF 218 XV60 BLACK 21N
TECHNYL® MAX AF 218 XV60 BLACK 21N
PA66
道默化学(DOMO Chemicals)
产品描述
TECHNYL MAX® AF 218 XV60 BLACK 21N is a high flow polyamide 66 resin, reinforced with 60% of glass fibre, heat stabilized, for injection moulding. Due to its outstanding flow characteristics, this grade shows exceptional processing behaviour, good surface aspect and reduced warpage of the finished part. The product offers a high stiffness and toughness balance combined with better multi-directional performance. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 高刚性热稳定良好表面低翘曲高流动填充增强 |
| 添加助剂 | 热稳定剂 |
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) |
| 颜色形状 | 粒状黑色 |
| 成型方式 | 注塑 |
| 增强填充 | 60% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.69 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
0.21 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) |
0.41 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
270 Mpa | ISO 527-1/-2 | Dry. |
断裂(brk) |
200 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | | | |
断裂(brk) |
2 % | ISO 527-1/-2 | Dry. |
断裂(brk) |
2.5 % | ISO 527-1/-2 | cond. |
弯曲强度 | | | |
- |
415 Mpa | ISO 178 | Dry. 2 mm/min |
- |
305 Mpa | ISO 178 | cond., 2 mm/min |
弯曲模量 | 19500 Mpa
| ISO 178 | Dry. 2 mm/min |
弯曲模量 | 15000 Mpa
| ISO 178 | cond., 2 mm/min |
拉伸模量 | 22000 Mpa
| ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 17400 Mpa
| ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
25 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) |
26 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
95 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) |
90 kJ/m² | ISO 179/1eU | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
255 °C | ISO 75 | |
熔融温度(Tm) | 263 °C
| ISO 11357-1 | 10°C/min |
加工温度 | 275~290 °C
| - | |
模具温度 | 80 °C
| - | |