Vydyne® 41H BK0677
PA66
奥升德(Ascend)
产品描述
Vydyne 41H BK0677 is an extrusion grade, impact-modified material aimed at fulfilling the specification requirements for cable-jacketing applications. The combination of its high-viscosity feedstock and impact modifier loading level imparts the toughness, abrasion resistance, low-temperature impact resilience and elongation properties needed for cable-jacketing applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击热稳定耐磨高粘度高熔体强度 | |||
| 添加助剂 | 抗冲击剂热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 挤出 | |||
| 增强填充 | 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.8 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 1.6 % | ISO 294-4 | 23°C, 2.00 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 49 Mpa | ISO 527-2 | Dry, 23°C |
断裂(brk) | 49 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 53 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 55 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 1800 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 1790 Mpa | ISO 527-2 | Dry, 23°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 83 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 100 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179 | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 41 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 85 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 56 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 75 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 75 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 75 °C | UL 746 | Dry |
电气Elec,0.75/0.8mm | 130 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 130 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 130 °C | UL 746 | Dry |
强度w/o impact,0.75/0.8mm | 115 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 120 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 125 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 150 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 120 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 262 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
HB | 3 mm | UL94 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 725 °C | IEC 60695-2-12 | Dry |
1.5mm | 725 °C | IEC 60695-2-12 | Dry |
3mm | 675 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.75mm | 750 °C | IEC 60695-2-13 | Dry |
1.5mm | 750 °C | IEC 60695-2-13 | Dry |
3.0mm | 700 °C | IEC 60695-2-13 | Dry |
燃烧速率 | 12 mm/min | ISO 3795 | Dry, 1.50 mm |
燃烧速率 | 7.9 mm/min | ISO 3795 | Dry, 3.00 mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-cm | IEC 60093 | Dry, 0.75 mm |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 14 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 2 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 2 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |