AKROMID® A3 1 S3 natural (2847)
AKROMID® A3 1 S3 natural (2847)
PA66
安科罗/开德阜(AKRO-PLASTIC)
产品描述
AKROMID® A3 1 S3 natural (2847) is an unreinforced, impact modified Polyamide 6.6. It is characterised by a medium dry impact strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 增韧/冲击改性热稳定 |
| 添加助剂 | 抗冲击剂热稳定剂 |
| 颜色形状 | 粒状本色 |
| 成型方式 | 注塑 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.11 g/cm³
| ISO 1183 | 23°C |
熔体体积流动速率(MVR) | | | |
275°C/5 kg |
55 cm³/10 min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
1.3~1.5 % | ISO 294-4 | |
横向(Across Flow) |
1.5~1.7 % | ISO 294-4 | |
吸湿率 | 2.5 %
| ISO 1110 | 70°C, 62% r.H. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
40 Mpa | ISO 527-2 | Cond., 50 mm/min |
屈服(yld) |
65 Mpa | ISO 527-2 | Dry, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
4.6 % | ISO 527-2 | Dry, 50 mm/min |
断裂(brk) |
100 % | ISO 527-2 | Cond., 50 mm/min |
断裂(brk) |
25 % | ISO 527-2 | Dry, 50 mm/min |
拉伸模量 | 1000 Mpa
| ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 2500 Mpa
| ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-40℃ (-40℉) |
8 kJ/m² | ISO 179-1/1eA | Dry |
23℃ (73℉) |
95 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) |
12 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
NB kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
194 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
60 °C | ISO 75/A | |
熔融温度(Tm) | 260 °C
| ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.6 mm | UL94 | |
FMVSS | + pass
| FMVSS 302 | > 1 mm Thickness |