Vydyne® R550HT BK02
PA66
奥升德(Ascend)
产品描述
Vydyne R550HT BK02 is a 50% glass-filled, heat-stabilized PA66 based resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance. Specifically designed for high-temperature applications, Vydyne R550HT BK02 can withstand elevated temperatures up to 190°C for an extended period of time.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性热稳定易脱模高流动填充增强 | |||
| 添加助剂 | 热稳定剂润滑剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.58 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.04 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 0.5 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 0.5 % | ISO 62 | 24 hr, 23°C |
吸水率 | 1.2 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 230 Mpa | ISO 527-2 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 2.3 % | ISO 527-2 | 23°C |
弯曲强度 | |||
- | 350 Mpa | ISO 178 | 23°C |
弯曲模量 | 16000 Mpa | ISO 178 | 23°C |
拉伸模量 | 17000 Mpa | ISO 527-2 | 23°C |
泊松比 | 0.4 - | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 14 kJ/m² | ISO 179 | |
23℃ (73℉) | 15 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 90 kJ/m² | ISO 179 | |
23℃ (73℉) | 95 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 16 kJ/m² | ISO 180 | |
23℃ (73℉) | 17 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 255 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 242 °C | ISO 75-2/A | Unannealed |
熔融温度(Tm) | 260 °C | ISO 11357-3 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
燃烧速率 | 0 mm/min | ISO 3795 | 2.00 mm, Self-Extinguishing |