| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.14 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
2.2 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) |
2 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 1.2 %
| ISO 62 | 24 hr, 23°C |
吸水率 | 2.4 %
| ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
55 Mpa | ISO 527-2 | Conditioned, 23°C |
屈服(yld) |
85 Mpa | ISO 527-2 | Dry, 23°C |
断裂(brk) |
40 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) |
55 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | | | |
屈服(yld) |
20 % | ISO 527-2 | Conditioned, 23°C |
屈服(yld) |
5 % | ISO 527-2 | Dry, 23°C |
标称断裂伸长率 |
50 % | ISO 527-2 | Conditioned, 23°C |
标称断裂伸长率 |
25 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | | | |
- |
30 Mpa | ISO 178 | Conditioned, 23°C |
- |
95 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 1000 Mpa
| ISO 178 | Conditioned, 23°C |
弯曲模量 | 2900 Mpa
| ISO 178 | Dry, 23°C |
拉伸模量 | 1800 Mpa
| ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 3100 Mpa
| ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 -
| ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
7 kJ/m² | ISO 179/1eA | Conditioned |
-30℃ (-22℉) |
5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) |
20 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) |
6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Conditioned |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
7 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) |
5 kJ/m² | ISO 180 | Dry |
23℃ (73℉) |
20 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) |
6 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
200 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
70 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | | | |
冲击w/impact,0.71mm |
95 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm |
110 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm |
110 °C | UL 746 | Dry |
电气Elec,0.71mm |
140 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm |
140 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm |
140 °C | UL 746 | Dry |
强度w/o impact,0.71mm |
115 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm |
125 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm |
125 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) |
100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C
| ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
V-2 |
0.71 mm | UL94 | Dry |
V-2 |
1.5 mm | UL94 | Dry |
V-2 |
3 mm | UL94 | Dry |
氧指数(LOI) | 24 %
| ISO 4589 | Dry |
灼热丝可燃性指数(GWFI) | | | |
0.71mm |
825 °C | IEC 60695-2-12 | Dry |
1.5mm |
825 °C | IEC 60695-2-12 | Dry |
3mm |
960 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | | | |
0.71mm |
700 °C | IEC 60695-2-13 | Dry |
1.5mm |
700 °C | IEC 60695-2-13 | Dry |
3.0mm |
700 °C | IEC 60695-2-13 | Dry |
紫外线暴露,水暴露试验和浸渍 | F1 -
| UL 746C | All Colors |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+18 Ohm-cm
| IEC 60093 | Dry, 0.75 mm |
相比漏电起痕指数(CTI ) | | | |
- |
400~599 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 20 kV/mm
| IEC 60243 | Dry, 0.75 mm |
耐电弧性 | 6 PLC
| ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 0 PLC
| UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC
| UL 746 | Dry, 0.71 mm |
热线圈起燃性(HWI) | 4 PLC
| UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 4 PLC
| UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | Dry, 0.71 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC
| UL 746 | Dry, 3.00 mm |