LNP™ THERMOCOMP™ RFZ349XC
LNP™ THERMOCOMP™ RFZ349XC
PA66
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP* RFZ349XC is a compound based on Nylon 66 resin containing 20% Glass Fiber, 15% Milled Glass. Added features of this material include: Flame Retardant.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 阻燃填充增强 |
| 添加助剂 | 阻燃剂 |
| 增强填充 | 20% 玻纤15% 研磨玻纤粉35% 玻纤+玻璃粉末 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.66 g/cm³
| ISO 1183 | |
收缩率 | | | |
纵向(Flow) |
0.39 % | ISO 294 | flow, 24 hrs |
纵向(Flow) |
0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
1.2 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) |
1.19 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.43 %
| ISO 62 | 23°C / 50% RH |
吸湿率 | 0.2 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
85 Mpa | ISO 527 | |
断裂(brk) |
124 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
断裂(brk) |
2.3 % | ASTM D638 | |
断裂(brk) |
3.2 % | ISO 527 | |
弯曲强度 | | | |
- |
179 Mpa | ASTM D790 | |
- |
197 Mpa | ISO 178 | |
弯曲模量 | 7170 Mpa
| ASTM D790 | |
弯曲模量 | 9000 Mpa
| ISO 178 | |
拉伸模量 | 11030 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 11400 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
64 J/m | ASTM D256 | |
23℃ (73℉) |
7 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
587 J/m | ASTM D4812 | |
23℃ (73℉) |
39 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)峰值 |
7 J | ASTM D3763 | |
多轴冲击 | 2 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
237 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
235 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |