Vydyne® 63H NT0752
PA66
奥升德(Ascend)
产品描述
Vydyne 63H NT0752 is a medium-viscosity, heat-stabilized PA66 resin suitable for injection-molding, extrusion and compounding applications. It is available in natural color only. Vydyne 63H NT0752 resin offers high strength, rigidity and toughness over a broad range of demanding applications, good fluid resistance to a wide variety of chemicals, solvents and oils, and heat stability to ensure property longevity when the material is subjected to higher temperatures.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高韧性热稳定耐化学性耐油耐溶剂中粘度高熔体强度 | |||
| 添加助剂 | 热稳定剂 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 1.9 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 8.5 % | ISO 62 | 24 hr, 23°C |
吸水率 | 2.5 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 85 Mpa | ISO 527-2 | Dry, 23°C |
断裂(brk) | 65 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 55 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
屈服(yld) | 20 % | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 5 % | ISO 527-2 | Dry, 23°C |
标称断裂伸长率 | 200 % | ISO 527-2 | Conditioned, 23°C |
标称断裂伸长率 | 25 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 20 Mpa | ISO 178 | Conditioned, 23°C |
- | 70 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 700 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 2500 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 1700 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 3200 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 179/1eA | Conditioned |
-30℃ (-22℉) | 5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 25 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Conditioned |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 5 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 25 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 6 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 190 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 68 °C | ISO 75-2/A | Dry, Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |