LNP™ THERMOCOMP™ RF00AH
PA66
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP RF00AH is a compound based on Nylon 66 resin containing 50% Glass Fiber. Added feature of this grade is: Healthcare.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 医疗级填充增强 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.6 g/cm³ | ISO 1183 | |
密度 | 1.6 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.37 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.3~0.5 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1.1~1.3 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.2 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.4 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 182 Mpa | ISO 527 | |
断裂(brk) | 166 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 7.8 % | ASTM D638 | |
断裂(brk) | 8.1 % | ISO 527 | |
弯曲强度 | |||
- | 262 Mpa | ASTM D790 | |
- | 265 Mpa | ISO 178 | |
弯曲模量 | 14470 Mpa | ASTM D790 | |
弯曲模量 | 14900 Mpa | ISO 178 | |
拉伸模量 | 17230 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 17810 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 96 J/m | ASTM D256 | |
23℃ (73℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 939 J/m | ASTM D4812 | |
23℃ (73℉) | 60 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 252 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 243 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 243 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 52.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 51 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 21.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 22 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |