TECHNYL® A 225F NATURAL
PA66
道默化学(DOMO Chemicals)
产品描述
TECHNYL® A 225F Natural is an unfilled polyamide 66, medium viscosity, for injection moulding, with a special crystallizing agent, for very fast cycles. This grade offers a good combination between primary properties of the unreinforced polyamide 66 and processing properties leading to increased productivity. These performances are associated with excellent dimensional stability, and excellent filling qualities. The UL94 V2 rating at 0.4mm makes that the product is particularly used in electrical applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 尺寸稳定短周期成型易填模中粘度 | |||
| 添加助剂 | 未指明添加剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.3 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1.3 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 1.1 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 70 Mpa | ISO 527-1/-2 | Dry. |
断裂(brk) | 50 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | |||
断裂(brk) | 20 % | ISO 527-1/-2 | Dry. |
断裂(brk) | 100 % | ISO 527-1/-2 | cond. |
弯曲强度 | |||
- | 125 Mpa | ISO 178 | Dry. 2 mm/min |
- | 55 Mpa | ISO 178 | cond., 2 mm/min |
弯曲模量 | 3150 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 1400 Mpa | ISO 178 | cond., 2 mm/min |
拉伸模量 | 3600 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 1600 Mpa | ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | cond. |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 200 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ISO 75 | |
熔融温度(Tm) | 263 °C | ISO 11357-1 | 10°C/min |
加工温度 | 265~285 °C | - | |
模具温度 | 60~80 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.4 mm | UL94 | |
V-2 | 0.75 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 700 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4.0E+13 Ohm-m | IEC 62631-3-1 | |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 22 kV/mm | IEC 60243-1 | 1 mm |