Ultramid® A3EG7
PA66
巴斯夫 (BASF)
产品描述
Ultramid A3EG7 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Applications
Typical applications include lamp socket housings, cooling fans, insulating profile for aluminium window frames, water containers for automotive cooling systems, as well as electrically insulating parts.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性绝缘尺寸稳定填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 35% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
比重 | 1.41 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 40 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.3 % | Internal | |
吸水率 | 1.6 % | ASTM D570 | 50% RH |
吸水率 | 5 % | ASTM D570 | Saturation |
吸水率 | 1.6 % | ISO 62 | 50% RH |
吸水率 | 5 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 150 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 210 Mpa | ISO 527 | Dry,23℃ |
断裂(brk) | 122 Mpa | ISO 527 | Dry,80℃ |
断裂(brk) | 207 Mpa | ASTM D638 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 5 % | ISO 527 | Conditioned,23℃ |
断裂(brk) | 3 % | ISO 527 | Dry,23℃ |
断裂(brk) | 5.3 % | ISO 527 | Dry,80℃ |
弯曲模量 | 9860 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 8400 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 10000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 8500 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 11500 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 22 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 14 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 75 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 105 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 95 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 96 J/m | ASTM D256 | Dry |
23℃ (73℉) | 123 J/m | ASTM D256 | Dry |
23℃ (73℉) | 14 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 250 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 250 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 250 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 250 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 120 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 120 °C | UL 746B | |
冲击w/impact,6.0mm | 120 °C | UL 746B | |
电气Elec,0.75/0.8mm | 120 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 120 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 120 °C | UL 746B | |
电气Elec,6.0mm | 120 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 130 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 130 °C | UL 746B | |
强度w/o impact,6.0mm | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 17 E-6/°C | Internal | Dry |
横向(Across Flow) | 65 E-6/°C | Internal | Dry |
- | 10 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 260 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 260 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
HB | 6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+10 Ohm-m | ASTM D257 | Conditioned,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.50 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | |
体积电阻率 | 1.0E+10 Ohm-m | IEC 60093 | Conditioned |
介电常数(DK) | |||
1MHz | 3.5 - | IEC 60250 | |
1MHz | 5.5 - | IEC 60250 | Conditioned |
耗散因数(DF) | |||
100Hz | 200 E-4 | IEC 60250 | |
100Hz | 3000 E-4 | IEC 60250 | Conditioned |
1MHz | 200 E-4 | IEC 60250 | |
1MHz | 1500 E-4 | IEC 60250 | Conditioned |
相比漏电起痕指数(CTI ) | |||
- | 550 V | IEC 60112 | Conditioned |
- | 550 V | IEC 60112 | Dry |