LNP™ LUBRICOMP™ RCL36S
PA66
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* RCL36S is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include:Electrically Conductive, Wear Resistant, Heat Stabilized.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定导电耐磨填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 30% 碳纤15% PTFE45% 碳纤+PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.38 g/cm³ | ISO 1183 | |
密度 | 1.38 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.11 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.1 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.7 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.72 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.84 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.53 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 245 Mpa | ISO 527 | |
断裂(brk) | 182 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 0.9 % | ASTM D638 | |
断裂(brk) | 1.8 % | ISO 527 | |
弯曲强度 | |||
- | 372 Mpa | ASTM D790 | |
- | 395 Mpa | ISO 178 | |
弯曲模量 | 18400 Mpa | ASTM D790 | |
弯曲模量 | 22700 Mpa | ISO 178 | |
拉伸模量 | 32400 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 22600 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.36 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.3 - | ASTM D 3702 | Static COF |
磨损因数 | 15 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 101 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1046 J/m | ASTM D4812 | |
23℃ (73℉) | 68 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 10 J | ASTM D3763 | |
多轴冲击 | 3 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 255 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 240 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |