Vydyne® R413H BK07
PA66
奥升德(Ascend)
产品描述
Vydyne R413H BK07 is general-purpose, heat-stabilized, impact-modified, 15% glass-fiber reinforced PA66 resin. Available in black, It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-fiber reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
Vydyne R413H BK07 is successfully used in a wide range of injection-molding engineering applications, including automotive clips, fasteners, brackets and carbon canisters; electrical connectors, housings, bobbins, etc.; and industrial gears, bearing shells, covers, housings, etc.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高冲击热稳定尺寸稳定抗蠕变易脱模耐化学性耐燃油耐油耐溶剂高流动填充增强 | |||
| 添加助剂 | 抗冲击剂热稳定剂润滑剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.21 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.7 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 0.8 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 1 % | ISO 62 | 24 hr, 23°C |
吸水率 | 1.9 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 80 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 110 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 13 % | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 5 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 73 Mpa | ISO 178 | Conditioned, 23°C |
- | 140 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 2800 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 4800 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 4100 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 5500 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 5 kJ/m² | ISO 179 | Conditioned |
-40℃ (-40℉) | 5 kJ/m² | ISO 179 | Dry |
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 6 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 18 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 12 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 70 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 75 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 76 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 80 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 9 kJ/m² | ISO 180 | Conditioned |
-40℃ (-40℉) | 9 kJ/m² | ISO 180 | Dry |
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 21 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 12 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 258 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 235 °C | ISO 75-2/A | Dry, Unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 30 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 110 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
HB | 3 mm | UL94 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+9 Ohm-cm | IEC 60093 | Dry, 0.75 mm |
相比漏电起痕指数(CTI ) | |||
- | 400~599 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 3 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 6 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 3 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.40 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746 | Dry, 0.40 mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746 | Dry, 3.00 mm |