Vydyne® R525J BK0722
PA66
奥升德(Ascend)
产品描述
R525J BK0722 is a black, 25% glass-filled, high-flow PA66 that is heat-stabilized with an electrically neutral heat stabilizer. It is specially designed for electrical applications requiring high dielectric strength, low conductivity and corrosion resistance.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度热稳定颜色稳定/易着色印刷/标记易脱模耐化学性高流动填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.32 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 0.9 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 0.9 % | ISO 62 | 24 hr, 23°C |
吸水率 | 2 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 117 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 174 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 7 % | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 3 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 150 Mpa | ISO 178 | Conditioned, 23°C |
- | 250 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 5700 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 7700 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 5500 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 8600 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 12 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 11 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 66 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 55 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 67 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 65 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 9 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 10 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 258 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 245 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 85 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 85 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746 | Dry |
电气Elec,0.75/0.8mm | 120 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 120 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 120 °C | UL 746 | Dry |
强度w/o impact,0.75/0.8mm | 115 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 120 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 120 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 110 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
HB | 3 mm | UL94 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm | IEC 60093 | Dry, 0.75 mm |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 24 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 5 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 1 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |
原材料现货供应:133-8218-6680(微信同号)