TECHNYL® A 218W V30 NATURAL
PA66
道默化学(DOMO Chemicals)
产品描述
TECHNYL® A 218W V30 Natural is a polyamide 66, reinforced with 30% of glass fibre, heat stabilized, for injection moulding. This grade offers an improved hydrolisis resistance, as well as an excellent combination between thermal and mechanical properties. It also restricts electrolytical corrosion. It is designed to be used in food contact and drinking water applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定食品接触级饮用水级耐水解耐腐蚀填充增强 | |||
| 添加助剂 | 热稳定剂耐水解剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.35 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1.1 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 0.8 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 190 Mpa | ISO 527-1/-2 | Dry. |
断裂(brk) | 125 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527-1/-2 | Dry. |
断裂(brk) | 7 % | ISO 527-1/-2 | cond. |
弯曲强度 | |||
- | 270 Mpa | ASTM D790 | Dry. 2 mm/min |
- | 135 Mpa | ASTM D790 | cond., 2 mm/min |
- | 275 Mpa | ISO 178 | Dry. 2 mm/min |
- | 217 Mpa | ISO 178 | cond., 2 mm/min |
弯曲模量 | 9000 Mpa | ASTM D790 | Dry. 2 mm/min |
弯曲模量 | 7000 Mpa | ASTM D790 | cond., 2 mm/min |
弯曲模量 | 9000 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 6300 Mpa | ISO 178 | cond., 2 mm/min |
拉伸模量 | 10000 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 7000 Mpa | ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | cond. |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 85 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 95 kJ/m² | ISO 179/1eU | cond. |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | 16 kJ/m² | ISO 180/1A | cond. |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 75 kJ/m² | ISO 180/1U | Dry |
23℃ (73℉) | 85 kJ/m² | ISO 180/1U | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 255 °C | ISO 75 | |
熔融温度(Tm) | 262 °C | ISO 11357-1 | 10°C/min |
加工温度 | 270~290 °C | - | |
模具温度 | 70~100 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 650 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 400 V | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 | 1 mm |