Zytel® ST801HS NC010
PA66
杜邦 (DuPont)
产品描述
Zytel® ST801HS NC010 is a heat stabilized Super Tough polyamide 66 resin. It offers outstanding impact resistance and high productivity.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高韧性增韧/冲击改性热稳定短周期成型 | |||
| 添加助剂 | 抗冲击剂热稳定剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 11.08 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.8 % | Internal | 3.2mm (0.126in) |
吸水率 | 1.2 % | ASTM D570 | Immersion 24h |
吸水率 | 6.7 % | ASTM D570 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 69 Mpa | ASTM D 638 | 50%RH,-40°C (-40°F) |
- | 41.4 Mpa | ASTM D 638 | 50%RH,23°C (73°F) |
- | 80 Mpa | ASTM D 638 | Dry, -40°C (-40°F) |
- | 34.5 Mpa | ASTM D 638 | Dry,121°C (250°F) |
- | 51.7 Mpa | ASTM D 638 | Dry,23°C (73°F) |
- | 40.7 Mpa | ASTM D 638 | Dry,77°C (170°F) |
拉伸延伸率 | |||
断裂(brk) | 10 % | ASTM D638 | 50%RH,-40°C (-40°F) |
断裂(brk) | 210 % | ASTM D638 | 50%RH,23°C (73°F) |
断裂(brk) | 170 % | ASTM D638 | 50%RH,77°C (170°F) |
断裂(brk) | 20 % | ASTM D638 | Dry, -40°C (-40°F) |
断裂(brk) | 275 % | ASTM D638 | Dry,121°C (250°F) |
断裂(brk) | 60 % | ASTM D638 | Dry,23°C (73°F) |
断裂(brk) | 220 % | ASTM D638 | Dry,77°C (170°F) |
弯曲模量 | 2344 Mpa | ASTM D790 | 50%RH,-40°C (-40°F) |
弯曲模量 | 324 Mpa | ASTM D790 | 50%RH,121°C (250°F) |
弯曲模量 | 862 Mpa | ASTM D790 | 50%RH,23°C (73°F) |
弯曲模量 | 393 Mpa | ASTM D790 | 50%RH,77°C (170°F) |
弯曲模量 | 1965 Mpa | ASTM D790 | Dry, -40°C (-40°F) |
弯曲模量 | 345 Mpa | ASTM D790 | Dry,121°C (250°F) |
弯曲模量 | 1689 Mpa | ASTM D790 | Dry,23°C (73°F) |
弯曲模量 | 476 Mpa | ASTM D790 | Dry,77°C (170°F) |
泊松比 | 0.41 - | - | 50%RH |
剪切强度 | 57.9 Mpa | ASTM D 732 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 139 J/m | ASTM D256 | 50%RH |
-40℃ (-40℉) | 160 J/m | ASTM D256 | Dry |
23℃ (73℉) | 1068 J/m | ASTM D256 | 50%RH |
23℃ (73℉) | 907 J/m | ASTM D256 | Dry |
拉伸冲击 | 1155 kJ/m² | ASTM D 1822 | 50%RH |
拉伸冲击 | 588 kJ/m² | ASTM D 1822 | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 89 R | ASTM D785 | 50%RH |
洛氏硬度R | 112 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 216 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 71 °C | ASTM D648 | Annealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 65 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 105 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746B | |
电气Elec,0.75/0.8mm | 130 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 130 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 130 °C | UL 746B | |
强度w/o impact,0.75/0.8mm | 95 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 105 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 110 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 120 E-6/°C | ASTM D 696 | 23 - 55°C |
熔融温度(Tm) | 263 °C | ASTM D3418 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
氧指数(LOI) | 19 % | ASTM D 2863 | 50%RH |
氧指数(LOI) | 18 % | ASTM D 2863 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm | ASTM D257 | 50%RH |
体积电阻率 | 1.0E+14 Ohm-cm | ASTM D257 | Dry |
介电常数(DK) | |||
100Hz | 5.5 - | ASTM D 150 | 50%RH |
100Hz | 3.2 - | ASTM D 150 | Dry |
1 kHz | 4.5 - | ASTM D 150 | 50%RH |
1 kHz | 3.2 - | ASTM D 150 | Dry |
1MHz | 3.2 - | ASTM D 150 | 50%RH |
1MHz | 2.9 - | ASTM D 150 | Dry |
耗散因数(DF) | |||
100Hz | 2000 E-4 | ASTM D 150 | 50%RH |
100Hz | 100 E-4 | ASTM D 150 | Dry |
1 kHz | 1000 E-4 | ASTM D 150 | 50%RH |
1 kHz | 100 E-4 | ASTM D 150 | Dry |
1MHz | 500 E-4 | ASTM D150 | 50%RH |
1MHz | 200 E-4 | ASTM D150 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | UL 746A | Dry,3.0mm |
耐电弧性 | 131 sec | ASTM D495 | Dry |
高电压电弧起痕速率(HVTR) | 7.6 mm/min | UL 746A | |
热线圈起燃性(HWI) | 9 sec | UL 746A | 0.75mm |
热线圈起燃性(HWI) | 14 sec | UL 746A | 1.5mm |
热线圈起燃性(HWI) | 18 sec | UL 746A | 3.0mm |
高电流弧起燃性(HAI) | 200 arcs | UL 746A | 0.75mm |
高电流弧起燃性(HAI) | 200 arcs | UL 746A | 1.5mm |
高电流弧起燃性(HAI) | 200 arcs | UL 746A | 3.0mm |