Tribocomp® PA66 LGF30 TS0 S8
PA66
索尔维(苏威)(Solvay)
产品描述
Tribocomp® PA66 LGF30 TS0 S8, is a 30% long glass fiber reinforced, black, high-flow PA66 with a pellet length of 8mm and 15% PTFE having excellent tribological performance. It can easily be processed on most injection molding machines.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定耐磨低摩擦高流动填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 长玻纤15% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.5 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | Dry |
吸水率 | 1.4 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 150 Mpa | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 95 Mpa | ISO 527-2 | Dry,120℃ |
断裂(brk) | 190 Mpa | ISO 527-2 | Dry,23℃ |
断裂(brk) | 120 Mpa | ISO 527-2 | Dry,90℃ |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527-2 | Dry |
弯曲强度 | |||
- | 200 Mpa | ISO 178 | Conditioned,23℃ |
- | 260 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 6200 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 8300 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 7900 Mpa | ISO 527-2 | Conditioned,23℃ |
拉伸模量 | 5500 Mpa | ISO 527-2 | Dry,120℃ |
拉伸模量 | 10500 Mpa | ISO 527-2 | Dry,23℃ |
拉伸模量 | 7100 Mpa | ISO 527-2 | Dry,90℃ |
摩擦系数 | 0.23 - | ASTM D 3702 | Dry,Dynamic |
摩擦系数 | 0.18 - | ASTM D 3702 | Dry,Static |
磨损因数 | 13 - | ASTM D 3702 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 19 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 179 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 255 °C | ISO 75-2/Bf | Dry,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 253 °C | ISO 75-2/Af | Dry,Unannealed |
线性膨胀系数(CLTE) | |||
- | 29 E-6 cm/cm/℃ | ISO 11359-2 | Dry |
导热系数 | 0.29 W/(m K) | ISO 22007 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1.0E+12 Ohm | ASTM D257 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 500 V | IEC 60112 | Dry |
绝缘强度 | 35 kV/mm | IEC 60243-1 | Dry,2.00mm |
原材料现货供应:133-8218-6680(微信同号)