Ultramid® A3EG7 EQ BK23189
PA66
巴斯夫 (BASF)
产品描述
Glass fiber reinforced injection molding grade for plastic parts in electronic components like housings for electronic control units or connectors. Ultramid EQ (Electronic Quality) materials offer a high purity regarding ionic and halogen containing compounds. This helps to minimize potential corrosion processes and to protect sensitive electronic components. The product has a LS coloration (Laser Sensitive) and can be marked with Nd:YAG lasers.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 印刷/标记填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 35% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.414 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 25 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.45 % | ISO 294-4 | |
横向(Across Flow) | 1.06 % | ISO 294-4 | |
- | 0.45 % | Internal | constrained |
吸水率 | 5.39 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 1.53 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 148 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
螺旋流 | 274 mm | - | d = 2.0 mm |
氯含量 | 2 ppm | Internal | Combustion IC |
溴含量 | 1 mg/kg | Internal | Combustion IC |
碘值 | 1 mg/kg | Internal | Combustion IC |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 130 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 195 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 6.2 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 3.3 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 215 Mpa | ISO 178 | Cond. |
- | 300 Mpa | ISO 178 | Dry |
弯曲模量 | 7600 Mpa | ISO 178 | Cond. |
弯曲模量 | 10700 Mpa | ISO 178 | Dry |
拉伸模量 | 7850 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 11100 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7.7 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 12.7 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 8.7 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 64 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 92 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 80 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 10.8 kJ/m² | ISO 180/A | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 250 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 260 °C | ISO 11357-1/-3 | |
加工温度 | 280~300 °C | - | injection moulding/extrusion |
模具温度 | 80~90 °C | - | Injection moulding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | IEC 60695-11-10 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | Dry |
表面电阻率 | 1.0E+15 Ohm | IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | |||
溶液A | 575 V | IEC 60112 | Cond. |