LNP™ LUBRICOMP™ RL0049S
PA66
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* RL0049S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Flame Retardant, Heat Stabilized, Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定阻燃耐磨 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 增强填充 | 20% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.53 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.52 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 1.5 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1.7 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.67 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.55 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.38 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 46 Mpa | ISO 527 | |
断裂(brk) | 47 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ASTM D638 | |
断裂(brk) | 2 % | ISO 527 | |
弯曲强度 | |||
- | 77 Mpa | ASTM D790 | |
- | 78 Mpa | ISO 178 | |
弯曲模量 | 3090 Mpa | ASTM D790 | |
弯曲模量 | 2970 Mpa | ISO 178 | |
拉伸模量 | 3170 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 3160 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 21 J/m | ASTM D256 | |
23℃ (73℉) | 2 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 170 J/m | ASTM D4812 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 95 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
原材料现货供应:133-8218-6680(微信同号)