TECHNYL® A 548B2 V15 BLACK 23N
PA66
道默化学(DOMO Chemicals)
产品描述
TECHNYL® A 548B2 V15 Black 23N is a polyamide 6.6, reinforced with 15% of glass fibre, heat stabilized, impact modified, for blow moulding. This grade offers an excellent long term Heat resistance and is suitable to work in environments characterized by a very high temperature. It has been also specially designed to be perfectly suitable for blow moulding processing.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性耐热热稳定耐热老化高粘度高熔体强度填充增强 | |||
| 添加助剂 | 抗冲击剂热稳定剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 吹塑 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.35 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 90 Mpa | ISO 527-1/-2 | Dry. |
断裂(brk) | 57 Mpa | ISO 527-1/-2 | cond. |
拉伸延伸率 | |||
断裂(brk) | 4.7 % | ISO 527-1/-2 | Dry. |
断裂(brk) | 8.8 % | ISO 527-1/-2 | cond. |
弯曲强度 | |||
- | 145 Mpa | ISO 178 | Dry. 2 mm/min |
弯曲模量 | 4500 Mpa | ISO 178 | Dry. 2 mm/min |
拉伸模量 | 4900 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
拉伸模量 | 3000 Mpa | ISO 527-1/-2 | cond., 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 14 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 79 kJ/m² | ISO 179/1eU | cond. |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75 | |
熔融温度(Tm) | 260 °C | ISO 11357-1 | 10°C/min |