TECHNYL® A 20 V35 BLACK 25
PA66
索尔维(苏威)(Solvay)
产品描述
TECHNYL® A 20 V35 Black 25 is a Red Phosphorous flame retardant polyamide 66, reinforced with 35% of glass fiber, heat stabilized, for injection moulding. This grade provides robust UL 94 V-0 and a full UL yellow card while offering good mechanical properties. This grade is suitable for moulding insulating parts for electrical devices, and more generally for thin parts under stress.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃填充增强 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 法规认证 | EN 45545(欧盟轨道交通防火测试)NF F 16-101(法国铁路防火测试)REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质)UL QMFZ2(UL认证) | |||
| 颜色形状 | 粒状本色黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 35% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.46 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.25 % | ISO 294-4 | Dry |
横向(Across Flow) | 1 % | ISO 294-4 | Dry |
吸水率 | 0.6 % | ISO 62 | 24 hr, 23°C |
吸水率 | 1.7 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 110 Mpa | ISO 527-2/1A | Conditioned,23℃ |
断裂(brk) | 175 Mpa | ISO 527-2/1A | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 3.2 % | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 2.1 % | ISO 527-2 | Dry,23℃ |
弯曲强度 | |||
- | 200 Mpa | ISO 178 | Conditioned,23℃ |
- | 260 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 7500 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 11000 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 8200 Mpa | ISO 527-2/1A | Conditioned,23℃ |
拉伸模量 | 12500 Mpa | ISO 527-2/1A | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 55 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 12 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 10 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 244 °C | ISO 75-2/Af | Dry,Annealed |
熔融温度(Tm) | 263 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | Dry |
V-0 | 1.6 mm | UL94 | Dry |
V-0 | 3.2 mm | UL94 | Dry |
氧指数(LOI) | 31 % | ISO 4589 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | Dry |
1.6mm | 960 °C | IEC 60695-2-12 | Dry |
3.2mm | 960 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
1.6mm | 725 °C | IEC 60695-2-13 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | Dry |
表面电阻率 | 1.0E+13 Ohm | IEC 60093 | Conditioned |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | Dry |
介电常数(DK) | |||
- | 4 - | IEC 60250 | Conditioned |
- | 3.4 - | IEC 60250 | Dry |
耗散因数(DF) | |||
- | 500 E-4 | IEC 60250 | Conditioned |
- | 200 E-4 | IEC 60250 | Dry |
相比漏电起痕指数(CTI ) | |||
溶液A | 400 V | IEC 60112 | Dry |
绝缘强度 | 32 kV/mm | IEC 60243-1 | Dry,0.8mm |