TECHNYL® ORANGE XA 1573 ORANGE 2688
PA66
道默化学(DOMO Chemicals)
产品描述
TECHNYL STAR® XA 1573 ORANGE 2688 is a polyamide 66 based on a non halogenated flame retardant system, reinforced with 30% of glass fiber, high flow, for injection moulding. This grade offers in addition to a high flow matrix and a good combination of fire properties the particularity to decrease the level of blooming/exudation phenomena during the lifetime of the application.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤良好表面低/无起霜耐腐蚀高流动低迁徙/析出填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 法规认证 | REACH (EC 1907/2006)RoHS(欧盟电子电气设备中有害物质) | |||
| 颜色形状 | 粒状橙色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.46 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
横向(Across Flow) | 1 % | ISO 294-4, 2577 | 72 hr, 23°C, 50% RH |
吸水率 | 4.1 % | ISO 62 | |
吸水率 | 0.7 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 130 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 2.7 % | ISO 527-1/-2 | Dry |
拉伸模量 | 11000 Mpa | ISO 527-1/-2 | Dry. 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 244 °C | ISO 75 | |
熔融温度(Tm) | 263 °C | ISO 11357-1 | 10°C/min |
加工温度 | 270~295 °C | - | |
模具温度 | 80 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.75 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 37 kV/mm | IEC 60243-1 | 1 mm |