Leona™ CR302
PA66
旭化成 (Asahi Kasei)
产品描述
Features: Electrically Conductive; Good Dimensional Stability, Filler-Mineral Uses: Electrical Parts; Electrical/Electronic Applications; Industrial Applications; Switches
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电尺寸稳定填充增强 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.52 g/cm³ | ISO 1183 | DRY |
比重 | 1.52 - | ASTM D792 | DRY |
收缩率 | |||
纵向(Flow) | 0.5~1 % | Internal | DRY |
吸水率 | 1.4 % | - | WET |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 140 Mpa | ISO 527 | DRY |
断裂(brk) | 92 Mpa | ISO 527 | WET |
- | 128 Mpa | ASTM D 638 | DRY |
- | 98 Mpa | ASTM D 638 | WET |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | DRY |
断裂(brk) | 3.5 % | ASTM D638 | WET |
断裂(brk) | 2 % | ISO 527 | DRY |
断裂(brk) | 2.5 % | ISO 527 | WET |
弯曲强度 | |||
- | 291 Mpa | ASTM D790 | DRY |
- | 157 Mpa | ASTM D790 | WET |
- | 197 Mpa | ISO 178 | DRY |
- | 148 Mpa | ISO 178 | WET |
弯曲模量 | 8800 Mpa | ASTM D790 | DRY |
弯曲模量 | 5800 Mpa | ASTM D790 | WET |
弯曲模量 | 9800 Mpa | ISO 178 | DRY |
弯曲模量 | 7100 Mpa | ISO 178 | WET |
拉伸模量 | 10000 Mpa | ISO 527 | DRY |
拉伸模量 | 7600 Mpa | ISO 527 | WET |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 4 kJ/m² | ISO 179 | DRY |
23℃ (73℉) | 5 kJ/m² | ISO 179 | WET |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 38 kJ/m² | ISO 179 | DRY |
23℃ (73℉) | 46 kJ/m² | ISO 179 | WET |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 36 J/m | ASTM D256 | DRY |
23℃ (73℉) | 39 J/m | ASTM D256 | WET |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 90 M | ASTM D 785 | DRY |
洛氏硬度 M | 90 M | ISO 2039 | DRY |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 250 °C | ASTM D648 | DRY |
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75 | DRY |
1.8 Mpa (264 psi)（18.6kg/cm²） | 245 °C | ASTM D648 | DRY |
1.8 Mpa (264 psi)（18.6kg/cm²） | 247 °C | ISO 75 | DRY |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | DRY |