Ultramid® D3WG12 HMG BK00102
PA66
巴斯夫 (BASF)
产品描述
Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish.
Applications
Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高强度高刚性良好表面填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 60% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.75 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.19 % | ISO 294-4 | |
横向(Across Flow) | 0.25 % | ISO 294-4 | |
吸水率 | 1 % | ISO 62 | Equilibrium, 23°C, 50% RH |
吸水率 | 2.5 % | ISO 62 | Saturation, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 220 Mpa | ISO 527 | Conditioned,23℃ |
断裂(brk) | 248 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ISO 527 | Conditioned,23℃ |
断裂(brk) | 2.5 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 351 Mpa | ISO 178 | Conditioned,23℃ |
- | 383 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 19400 Mpa | ISO 178 | Conditioned,23℃ |
弯曲模量 | 18900 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 20830 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 20200 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 12 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 13 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 85 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 95 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 93 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 99 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 11 kJ/m² | ISO 180 | Conditioned |
-40℃ (-40℉) | 12 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 13 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 13 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 224 °C | ISO 75 | Dry |
熔融温度(Tm) | 260 °C | ISO 3146 | Dry |