Vydyne® R525H BLK
PA66
奥升德(Ascend)
产品描述
Vydyne R525H BLK is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R525H BLK is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R525H BLK has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses
Vydyne R525H BLK resin is used for under-the-hood automotive applications. Its hydrolysis-resistant properties make R525H BLK an excellent candidate for radiator end tank and heater core applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐疲劳热稳定耐化学性耐水解耐燃油耐溶剂耐防冻剂高流动填充增强 | |||
| 添加助剂 | 热稳定剂润滑剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.32 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 0.9 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 0.9 % | ISO 62 | 24 hr, 23°C |
吸水率 | 2 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 117 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 174 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 7 % | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 3 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 150 Mpa | ISO 178 | Conditioned, 23°C |
- | 250 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 5700 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 7700 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 5500 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 8600 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 10 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 12 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 11 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 66 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 55 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 67 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 65 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 9 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 10 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 258 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 245 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 120 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 120 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 120 °C | UL 746 | Dry |
电气Elec,0.75/0.8mm | 140 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 140 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 140 °C | UL 746 | Dry |
强度w/o impact,0.75/0.8mm | 125 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 140 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 140 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 110 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
HB | 3 mm | UL94 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 675 °C | IEC 60695-2-12 | Dry |
1.5mm | 675 °C | IEC 60695-2-12 | Dry |
3mm | 675 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.75mm | 700 °C | IEC 60695-2-13 | Dry |
1.5mm | 700 °C | IEC 60695-2-13 | Dry |
3.0mm | 700 °C | IEC 60695-2-13 | Dry |
燃烧速率 | 0 mm/min | ISO 3795 | Dry, 2.00 mm, Self-Extinguishing |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm | IEC 60093 | Dry, 0.75 mm |
相比漏电起痕指数(CTI ) | |||
- | 250~399 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 20 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 6 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 1 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |