Vydyne® R533T
PA66
奥升德(Ascend)
产品描述
Vydyne R533T is a translucent 33% glass-fiber reinforced PA66 resin designed specifically for use in power-steering reservoirs and other applications where chemical resistance, whiteness and transmittance are required.
Vydyne R533T resin has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度耐化学性填充增强 | |||
| 颜色形状 | 粒状半透明 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 33% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 0.9 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 0.8 % | ISO 62 | 24 hr, 23°C |
吸水率 | 1.8 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 150 Mpa | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 210 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
断裂(brk) | 6 % | ISO 527-2 | Conditioned, 23°C |
断裂(brk) | 4 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 205 Mpa | ISO 178 | Conditioned, 23°C |
- | 290 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 6500 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 9500 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 7900 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 10200 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | 8 kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 14 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | 12 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 86 kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | NB kJ/m² | ISO 179 | Dry |
23℃ (73℉) | 90 kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | 10 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 14 kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | 12 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 252 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 235 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 100 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 100 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 100 °C | UL 746 | Dry |
电气Elec,0.75/0.8mm | 120 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 120 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 120 °C | UL 746 | Dry |
强度w/o impact,0.75/0.8mm | 125 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 125 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 125 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 22 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 110 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 264 °C | ISO 11357-3 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Dry |
HB | 1.5 mm | UL94 | Dry |
HB | 3 mm | UL94 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 750 °C | IEC 60695-2-12 | Dry |
1.5mm | 725 °C | IEC 60695-2-12 | Dry |
3mm | 800 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.75mm | 775 °C | IEC 60695-2-13 | Dry |
1.5mm | 725 °C | IEC 60695-2-13 | Dry |
3.0mm | 750 °C | IEC 60695-2-13 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-cm | IEC 60093 | Dry, 3.00 mm |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 20 kV/mm | IEC 60243 | Dry, 1.00 mm |
耐电弧性 | 5 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 1 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 23 % | ASTM D1003 | Dry |