Vydyne® 25WSP
PA66
奥升德(Ascend)
产品描述
Vydyne 25WSP is a black, weather-resistant injection-molding grade PA66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength, rigidity, good toughness, high melt point, good surface lubricity and abrasion resistance. Vydyne 25WSP maintains the chemical resistance typical of PA66 to many chemicals, machine and motor oils, solvents and gasoline.
Weather resistance is obtained by incorporating finely divided, well-dispersed carbon black particles in the PA66 matrix. While the presence of carbon black usually increases brittleness, this resin has been formulated to minimize loss of ductility properties such as elongation and Izod impact strength. As a result, parts molded from 25WSP frequently exhibit higher ductility and practical toughness compared with other black, weather-resistant, non-impact-modified PA66 molded parts.
Vydyne 25WSP resin is internally and externally lubricated for improved machine feed and exceptional mold release. Vydyne 25WSP is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because molded parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 25WSP can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis.
Typical Applications/End Uses:
Lubricated for machine feed and mold release, Vydyne 25WSP provides very good flow and easy moldability. Typical applications include cable ties/tie straps, where its combination of easy flow, good ductility and high tensile strength is particularly attractive, and a wide variety of electrical/electronic and miscellaneous applications requiring weather resistance.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高强度高刚性耐磨短周期成型易脱模耐候性耐化学性耐燃油耐油耐溶剂 | |||
添加助剂 | 润滑剂 | |||
法规认证 | MIL M-20693B(美国军用标准) | |||
成型方式 | 注塑 | |||
增强填充 | 炭黑 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.6 % | ISO 294-4 | 23°C, 2.00 mm |
横向(Across Flow) | 1.4 % | ISO 294-4 | 23°C, 2.00 mm |
吸水率 | 1.2 % | ISO 62 | 24 hr, 23°C |
吸水率 | 2.4 % | ISO 62 | Equilibrium, 23°C, 50% RH |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 77 Mpa | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 83 Mpa | ISO 527-2 | Dry, 23°C |
拉伸延伸率 | |||
屈服(yld) | 25 % | ISO 527-2 | Conditioned, 23°C |
屈服(yld) | 4.5 % | ISO 527-2 | Dry, 23°C |
标称断裂伸长率 | 60 % | ISO 527-2 | Conditioned, 23°C |
标称断裂伸长率 | 20 % | ISO 527-2 | Dry, 23°C |
弯曲强度 | |||
- | 22 Mpa | ISO 178 | Conditioned, 23°C |
- | 87 Mpa | ISO 178 | Dry, 23°C |
弯曲模量 | 1400 Mpa | ISO 178 | Conditioned, 23°C |
弯曲模量 | 3100 Mpa | ISO 178 | Dry, 23°C |
拉伸模量 | 1550 Mpa | ISO 527-2 | Conditioned, 23°C |
拉伸模量 | 3400 Mpa | ISO 527-2 | Dry, 23°C |
泊松比 | 0.4 - | ISO 527-2 | Dry |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4.8 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 180 | Dry |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 225 °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 70 °C | ISO 75-2/A | Dry, Unannealed |
相对温度指数(RTI) | |||
冲击w/impact,0.75/0.8mm | 75 °C | UL 746 | Dry |
冲击w/impact,1.5/1.6 mm | 75 °C | UL 746 | Dry |
冲击w/impact,3.0/3.2 mm | 75 °C | UL 746 | Dry |
电气Elec,0.75/0.8mm | 130 °C | UL 746 | Dry |
电气Elec,1.5/1.6 mm | 130 °C | UL 746 | Dry |
电气Elec,3.0/3.2 mm | 130 °C | UL 746 | Dry |
强度w/o impact,0.75/0.8mm | 85 °C | UL 746 | Dry |
强度w/o impact,1.5/1.6 mm | 85 °C | UL 746 | Dry |
强度w/o impact,3.0/3.2 mm | 85 °C | UL 746 | Dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 100 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
横向(Across Flow) | 110 E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
熔融温度(Tm) | 260 °C | ISO 11357-3 | Dry |
燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.75 mm | UL94 | Dry |
V-2 | 1.5 mm | UL94 | Dry |
V-2 | 3 mm | UL94 | Dry |
氧指数(LOI) | 23 % | ISO 4589 | Dry |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 850 °C | IEC 60695-2-12 | Dry |
1.5mm | 875 °C | IEC 60695-2-12 | Dry |
3mm | 960 °C | IEC 60695-2-12 | Dry |
灼热丝点燃温度(GWIT) | |||
0.75mm | 700 °C | IEC 60695-2-13 | Dry |
1.5mm | 700 °C | IEC 60695-2-13 | Dry |
3.0mm | 725 °C | IEC 60695-2-13 | Dry |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | Black |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry, 3.00 mm |
绝缘强度 | 26 kV/mm | IEC 60243 | Dry, 0.75 mm |
耐电弧性 | 5 PLC | ASTM D495 | Dry, 3.00 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746 | Dry |
热线圈起燃性(HWI) | 4 PLC | UL 746 | Dry, 0.75 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | Dry, 1.50 mm |
热线圈起燃性(HWI) | 2 PLC | UL 746 | Dry, 3.00 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 1.50 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | Dry, 3.00 mm |