Leona™ 90G33
PA66
旭化成 (Asahi Kasei)
产品描述
Features: High Flow; High Stiffness; High Strength; Pleasing Surface Appearance, Glass Fiber, 33% Uses: Automotive Applications; Automotive Interior Parts; Industrial Applications; Structural Parts
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性良好表面高流动 | |||
| 增强填充 | 33% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.39 g/cm³ | ISO 1183 | DRY |
比重 | 1.39 - | ASTM D792 | DRY |
收缩率 | |||
纵向(Flow) | 0.4~0.9 % | Internal | DRY |
吸水率 | 1.4 % | - | WET |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 180 Mpa | ISO 527 | DRY |
断裂(brk) | 150 Mpa | ISO 527 | WET |
- | 194 Mpa | ASTM D 638 | DRY |
- | 157 Mpa | ASTM D 638 | WET |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | DRY |
断裂(brk) | 4 % | ASTM D638 | WET |
断裂(brk) | 2.5 % | ISO 527 | DRY |
断裂(brk) | 3 % | ISO 527 | WET |
弯曲强度 | |||
- | 294 Mpa | ASTM D790 | DRY |
- | 245 Mpa | ASTM D790 | WET |
- | 238 Mpa | ISO 178 | DRY |
- | 216 Mpa | ISO 178 | WET |
弯曲模量 | 9600 Mpa | ASTM D790 | DRY |
弯曲模量 | 7600 Mpa | ASTM D790 | WET |
弯曲模量 | 10000 Mpa | ISO 178 | DRY |
弯曲模量 | 8100 Mpa | ISO 178 | WET |
拉伸模量 | 10200 Mpa | ISO 527 | DRY |
拉伸模量 | 9300 Mpa | ISO 527 | WET |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 179 | DRY |
23℃ (73℉) | 12 kJ/m² | ISO 179 | WET |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 55 kJ/m² | ISO 179 | DRY |
23℃ (73℉) | 54 kJ/m² | ISO 179 | WET |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 98 J/m | ASTM D256 | DRY |
23℃ (73℉) | 118 J/m | ASTM D256 | WET |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 90 M | ASTM D 785 | DRY |
洛氏硬度 M | 90 M | ISO 2039 | DRY |
洛氏硬度R | 120 R | ASTM D785 | DRY |
洛氏硬度R | 120 R | ISO 2039 | DRY |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 235 °C | ISO 75 | DRY |
1.8 Mpa (264 psi)（18.6kg/cm²） | 220 °C | ASTM D648 | DRY |
1.8 Mpa (264 psi)（18.6kg/cm²） | 220 °C | ISO 75 | DRY |
线性膨胀系数(CLTE) | |||
- | 30 E-6/K | ASTM D 696 | DRY |