LNP™ LUBRICOMP™ RAL22S
PA66
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP RAL22S is a compound based on Nylon 66 resin containing 10% PTFE, 10% Aramid. Added features of this material include: Wear Resistant.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 耐磨填充增强 | |||
增强填充 | 10% 芳纶纤维10% PTFE |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.22 g/cm³ | ISO 1183 | |
密度 | 1.22 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.92 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 1.9 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 2 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.95 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.7 % | ASTM D 570 | 50% RH, 24 hrs |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 79 Mpa | ISO 527 | |
断裂(brk) | 81 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 8.1 % | ASTM D638 | |
断裂(brk) | 9.5 % | ISO 527 | |
弯曲强度 | |||
- | 110 Mpa | ASTM D790 | |
- | 117 Mpa | ISO 178 | |
弯曲模量 | 2960 Mpa | ASTM D790 | |
弯曲模量 | 3500 Mpa | ISO 178 | |
拉伸模量 | 3440 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 3500 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.55 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.46 - | ASTM D 3702 | Static COF |
磨损因数 | 13 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 133 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 747 J/m | ASTM D4812 | |
23℃ (73℉) | 48 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 6 J | ASTM D3763 | |
多轴冲击 | 1 J | ISO 6603 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 248 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 198 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 193 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 73.8 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 73.6 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 82.8 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 82.6 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |