LNP™ THERMOCOMP™ RF008H
PA66
沙特基础 (SABIC)
产品描述
LNP* THERMOCOMP* RF008H is a compound based on Nylon 66 containing 40% Glass Fiber. Added feature of this grade is: Healthcare.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 医疗级填充增强 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.47 g/cm³ | ISO 1183 | |
密度 | 1.478 g/cm³ | ASTM D792 | |
比重 | 1.5 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.2~0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1~3 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.97 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.6 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 188 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 184 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2.7 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 275 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 287 Mpa | ISO 178 | |
弯曲模量 | 10410 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 12100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 13300 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 12200 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 117 J/m | ASTM D256 | |
23℃ (73℉) | 13 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1137 J/m | ASTM D4812 | |
23℃ (73℉) | 74 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 10 J | ASTM D3763 | |
多轴冲击 | 3 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 252 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 240 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25.2 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 26.8 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 57.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 59.2 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |