AKROMID® A3 GF 50 6 black (6860)
PA66
安科罗/开德阜(AKRO-PLASTIC)
产品描述
KROMID® A3 GF 50 6 black (6860) is a 50% glass fiber reinforced polyamide 6.6. It is characterised by a very high stiffness and strength. Furthermore, the material is anorganically high heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry, e.g. gearbox components.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性热稳定填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.57 g/cm³ | ISO 1183 | 23°C |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294-4 | |
横向(Across Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 3.7~4.3 % | ISO 62 | 23°C saturated |
吸湿率 | 1.3~1.5 % | ISO 1110 | 70°C, 62% r.H. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 180 Mpa | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 250 Mpa | ISO 527-2 | Dry, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.7 % | ISO 527-2 | Cond., 5 mm/min |
断裂(brk) | 2.7 % | ISO 527-2 | Dry, 5 mm/min |
拉伸模量 | 14000 Mpa | ISO 527-2 | Cond., 1 mm/min |
拉伸模量 | 18000 Mpa | ISO 527-2 | Dry, 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 23 kJ/m² | ISO 179-1/1eA | Cond. |
23℃ (73℉) | 19 kJ/m² | ISO 179-1/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 110 kJ/m² | ISO 179-1/1eU | Cond. |
23℃ (73℉) | 105 kJ/m² | ISO 179-1/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 260 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 260 °C | ISO 75/A | |
熔融温度(Tm) | 262 °C | ISO 11357-3 | DSC, 10K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
FMVSS | + pass | FMVSS 302 | > 1 mm Thickness |