LNP™ THERMOCOMP™ RF008XXH
LNP™ THERMOCOMP™ RF008XXH
PA66
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP RF008XXH is a compound based on Nylon 66 resin containing 40% Glass Fiber. Added feature of this material includes: Healthcare.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 医疗级填充增强 |
| 增强填充 | 40% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.48 g/cm³
| ASTM D792 | |
比重 | 1.5 -
| ASTM D792 | |
收缩率 | | | |
纵向(Flow) |
0.2~0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) |
1~3 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 1 %
| ISO 62 | 23°C / 50% RH |
吸湿率 | 0.66 %
| ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
232 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
210 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
2.9 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
2.9 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
断裂(brk) |
337 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
229 Mpa | ISO 178 | |
弯曲模量 | 12400 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 11170 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 13900 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 14060 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
166 J/m | ASTM D256 | |
23℃ (73℉) |
16 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
1320 J/m | ASTM D4812 | |
23℃ (73℉) |
86 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
18 J | ASTM D3763 | |
多轴冲击 | 4 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
260 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
259 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
253 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
244 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
32 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) |
62 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |