Celstran® PA66-GF50-02 AF3001 Natural
PA66
塞拉尼斯(Celanese)
产品描述
PA66 with 50 % ash content - heat stabilized -11mm
Material code according to ISO 1043-1: PA66 Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 高强度高刚性高冲击耐低温冲击耐热热稳定低翘曲抗蠕变填充增强 | |||
添加助剂 | 热稳定剂 | |||
颜色形状 | 粒状本色 | |||
成型方式 | 注塑 | |||
增强填充 | 50% 长玻纤 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.56 g/cm³ | ISO 1183 | |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 260 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
- | 425 Mpa | ISO 178 | 23°C |
弯曲模量 | 14700 Mpa | ISO 178 | 23°C |
拉伸模量 | 16500 Mpa | ISO 527-2/1A | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 49 kJ/m² | ISO 179/1eA | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | 261 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 260 °C | ISO 11357-1/-3 | 10°C/min |