LNP™ LUBRICOMP™ REL22
PA66
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP REL22 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Electrically Conductive.
基本信息
原厂资料 | 物性表(英文) | |||
产品特性 | 导电耐磨填充增强 | |||
增强填充 | 10% 碳纤10% PTFE20% 碳纤+PTFE |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.246 g/cm³ | ASTM D792 | |
比重 | 1.25 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.3~0.5 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1~3 % | ASTM D 955 | xflow, 24 hrs |
吸湿率 | 1.2 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.81 % | ASTM D 570 | 50% RH, 24 hrs |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 2 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 170 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 173 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.8 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2.6 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 241 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 230 Mpa | ISO 178 | |
弯曲模量 | 8260 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 7920 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 10500 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 9960 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.49 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.49 - | ASTM D 3702 | Static COF |
磨损因数 | 0 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Ring |
磨损因数 | 36 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 50 J/m | ASTM D256 | |
23℃ (73℉) | 5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 514 J/m | ASTM D4812 | |
23℃ (73℉) | 32 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 6 J | ASTM D3763 | |
多轴冲击 | 1 J | ISO 6603 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 261 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)(4.6kg/cm²) | 260 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)(18.6kg/cm²) | 253 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)(18.6kg/cm²) | 248 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 38 E-6/°C | ASTM D 696 | -30°C to 30°C, flow |
横向(Across Flow) | 76 E-6/°C | ASTM D 696 | -30°C to 30°C, xflow |