RTP 204 FR
PA66
安特普工程塑料(RTP Company)
产品描述
The RTP series of flame retardant, glass fiber reinforced nylon materials are designed to provide the optimal balance of strength, electrical and ignition resistance properties while exhibiting excellent processing characteristics. RTP 204 FR possesses UL94 V-0 certification, as well as a complete range of UL94 electrical ratings and RTI assignment required for many EEE applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃易成型填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.64 g/cm3 | ASTM D792 | |
收缩率 | |||
- | 0.2~0.3 % | ASTM D 955 | 3.2 mm |
吸水率 | 0.7 % | ASTM D570 | 24 hrs, 23°C |
填充/灰分 | 25 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 141 Mpa | ASTM D 638 | |
拉伸延伸率 | |||
- | 2~3 % | ASTM D 638 | |
弯曲强度 | |||
- | 214 Mpa | ASTM D790 | |
弯曲模量 | 9101 Mpa | ASTM D790 | |
拉伸模量 | 10342 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 96 J/m | ASTM D 256 | 3.2 mm |
悬臂梁无缺口(Izod Unnotched) | |||
- | 747 J/m | ASTM D 4812 | 3.2 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 246 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm2） | 229 °C | ASTM D648 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | |
氧指数(LOI) | 34 % | ASTM D 2863 | |
灼热丝可燃性指数(GWFI) | |||
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
3.0mm | 775 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+14 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
1MHz | 3.8 - | ASTM D 150 | Dry |
耗散因数(DF) | |||
1MHz | 150 E-4 | ASTM D150 | Dry |
绝缘强度 | 18.7 kV/mm | ASTM D149 | S/T, in oil |