INVISTA U4630HSL
PA66
英威达(INVISTA)
产品描述
INVISTA U4630HSL is a heat-stabilized, lubricated PA66 resin in natural color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications. It is lubricated internally and externally.
Features
? Excellent property retention at elevated temperatures
? Improved flow and processability
Classification
ASTM D4066 classification PA0121
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定润滑的易成型 | |||
| 添加助剂 | 热稳定剂润滑剂 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm3 | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.7 % | ISO 294-4 | 2.0 mm |
横向(Across Flow) | 1.7 % | ISO 294-4 | 2.0 mm |
吸水率 | 1.7 % | ISO 62 | 24 hours |
吸水率 | 2.6 % | ISO 62 | equilibrium @ 50% RH |
粘度 | 134 cm3/g | ISO 307 | VN at 0.5% in formic acid, nominal |
粘度 | 147 cm3/g | ISO 307 | VN at 0.5% in sulfuric acid, nominal |
粘度 | 2.65 - | Internal | RV at 1% in sulfuric acid, nominal |
粘度 | 46 - | ASTM D 789 | RV in formic acid, nominal |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 84 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 4.4 % | ISO 527 | |
断裂(brk) | 30 % | ISO 527 | |
弯曲强度 | |||
- | 94 Mpa | ISO 178 | |
弯曲模量 | 2900 Mpa | ISO 178 | |
拉伸模量 | 3100 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4.2 kJ/m2 | ISO 179 | |
23℃ (73℉) | 5 kJ/m2 | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m2 | ISO 179 | |
23℃ (73℉) | NB kJ/m2 | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5 kJ/m2 | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 185 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm2） | 62 °C | ISO 75 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 90 E-6/°C | ISO 11359 | 23 - 55 °C |
横向(Across Flow) | 90 E-6/°C | ISO 11359 | 23 - 55 °C |
熔融温度(Tm) | 261 °C | ISO 11357 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.4 mm | UL94 | |
V-2 | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.71mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | 3.0 mm |
绝缘强度 | 18 kV/mm | IEC 60243 | 1.0 mm |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746A | |
高压低流耐电弧性(HVAR) | 5 PLC | UL 746A |