INVISTA HV240A
PA66
英威达(INVISTA)
产品描述
INVISTA HV240A is a high viscosity PA66 resin for extrusion, injection molding, and compounding applications. It is non-lubricated and has excellent whiteness.
Features
? High viscosity
? Excellent whiteness and processability
? Fast and consistent crystallization
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高粘度 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 成型方式 | 注塑挤出共混改性 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm3 | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.3 % | ISO 294-4 | 2.0 mm |
横向(Across Flow) | 1.5 % | ISO 294-4 | 2.0 mm |
吸水率 | 1.8 % | ISO 62 | 24 hours |
吸水率 | 2.7 % | ISO 62 | equilibrium @ 50% RH |
粘度 | 295 cm3/g | ISO 307 | VN at 0.5% in formic acid, nominal |
粘度 | 300 cm3/g | ISO 307 | VN at 0.5% in sulfuric acid, nominal |
粘度 | 4.6 - | Internal | RV at 1% in sulfuric acid, nominal |
粘度 | 240 - | ASTM D 789 | RV in formic acid, nominal |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 84 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 4.2 % | ISO 527 | |
断裂(brk) | 50 % | ISO 527 | |
弯曲强度 | |||
- | 100 Mpa | ISO 178 | |
弯曲模量 | 2900 Mpa | ISO 178 | |
拉伸模量 | 3150 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6.4 kJ/m2 | ISO 179 | |
23℃ (73℉) | 6.2 kJ/m2 | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m2 | ISO 179 | |
23℃ (73℉) | NB kJ/m2 | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.5 kJ/m2 | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 206 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm2） | 72 °C | ISO 75 | |
熔融温度(Tm) | 262 °C | ISO 11357 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | |
HB | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.01E+3 Ohm-cm | IEC 60093 | 2.0 mm |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | 3.0 mm |
绝缘强度 | 10.8 kV/mm | IEC 60243 | 1.0 mm |