Ultramid® B3WGM35 R03 UN
PA6
巴斯夫 (BASF)
产品描述
Heat stabilised, 40 % glass fibre and mineral reinforced polyamide 6 injection moulding compound with very good flow properties, excellent dimensional stability, low warp and low sink mark visibility. It is ideally suited for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds, mirror housings, appliance components as well as interior and exterior door handles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定尺寸稳定低翘曲良好流动性填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 15% 玻纤25% 矿物40% 玻纤+矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.47 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
275°C/5 kg | 80 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.35 % | ISO 294-4 | |
横向(Across Flow) | 0.8 % | ISO 294-4 | |
- | 0.35 % | Internal | constrained |
粘度 | 110 cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 65 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 120 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 9.5 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 3 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 115 Mpa | ISO 178 | Cond. |
- | 190 Mpa | ISO 178 | Dry |
弯曲模量 | 4100 Mpa | ISO 178 | Cond. |
弯曲模量 | 8000 Mpa | ISO 178 | Dry |
拉伸模量 | 4300 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 8300 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3.5 kJ/m² | ISO 179/1eA | Cond. |
-30℃ (-22℉) | 3.5 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 7.5 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 40 kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | 45 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | 50 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 215 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 195 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | DSC |
加工温度 | 250~290 °C | - | Injection moulding/Extrusion |
模具温度 | 80~95 °C | - | Injection moulding |