产品描述
High modulus, high strength and excellent thermal distortion stability are the key features of Ultrasint PA6 X043 black. These properties ensure precise feature control, very good mechanical properties and simple surface reprocessing of 3D printed parts, in particular for complex shapes or structures. Parts built of this material have similar properties to those of injection molded PA6.
Ultrasint PA6 X043 black can fulfill the requirements of functional applications regarding high accuracy and mechanical strength as well as a high heat distortion temperature - properties, where existing 3D printing materials often show limitations.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度热稳定 | |||
| 颜色形状 | 粉末状黑色 | |||
| 成型方式 | 激光烧结(SLS)3D打印 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.15 g/cm³ | ISO 1183 | Printed Part |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | 57 cm³/10 min | ISO 1133 | |
粒子大小 | 42 micrometer | Internal | d10 |
粒子大小 | 62 micrometer | Internal | d50 |
粒子大小 | 88 micrometer | Internal | d90 |
堆积(视)密度 | 0.54 g/cm³ | ISO 696 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 70 Mpa | ISO 527-2 | x-direction |
- | 67 Mpa | ISO 527-2 | z-direction |
拉伸延伸率 | |||
断裂(brk) | 5.6 % | ISO 527-2 | x-direction |
断裂(brk) | 3.3 % | ISO 527-2 | z-direction |
弯曲强度 | |||
- | 105 Mpa | ISO 178 | x-direction |
- | 103 Mpa | ISO 178 | z-direction |
弯曲应变 | |||
断裂(brk) | 6.1 % | ISO 178 | x-direction |
断裂(brk) | 6.1 % | ISO 178 | z-direction |
弯曲模量 | 2950 Mpa | ISO 178 | x-direction |
弯曲模量 | 2950 Mpa | ISO 178 | z-direction |
拉伸模量 | 3500 Mpa | ISO 527-2 | x-direction |
拉伸模量 | 3400 Mpa | ISO 527-2 | z-direction |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 5 kJ/m² | ISO 179 | x-direction |
- | 5.5 kJ/m² | ISO 179 | z-direction |
简支梁无缺口(Charpy Unnotched) | |||
- | 93.6 kJ/m² | ISO 179 | x-direction |
- | 72.2 kJ/m² | ISO 179 | z-direction |
悬臂梁缺口(Izod Notched) | |||
- | 5.9 kJ/m² | ISO 180 | x-direction |
- | 5.1 kJ/m² | ISO 180 | z-direction |
悬臂梁无缺口(Izod Unnotched) | |||
- | 84.3 kJ/m² | ISO 180 | x-direction |
- | 59.9 kJ/m² | ISO 180 | z-direction |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 218 °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 221 °C | ISO 306 | 10 N |
维卡软化温度(Vicat) | 216 °C | ISO 306 | 50 N |
熔融温度(Tm) | 223 °C | ISO 11357 | 20 K/min |
结晶温度 | 197 °C | ISO 11357 | 20 K/min |