Ultramid® B3EG6 EQ BK 23189
Ultramid® B3EG6 EQ BK 23189
PA6
巴斯夫 (BASF)
产品描述
Glass fiber reinforced injection molding grade for plastic parts in electronic components like housings for electronic control
units or connectors. Ultramid EQ (Electronic Quality) materials offer a high purity regarding ionic and halogen containing
compounds. This helps to minimize potential corrosion processes and to protect sensitive electronic components.
The black colored product has a LS coloration (Laser Sensitive) and can be marked with Nd:YAG lasers
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 印刷/标记填充增强 |
| 颜色形状 | 粒状黑色 |
| 成型方式 | 注塑 |
| 增强填充 | 30% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.358 g/cm³
| ISO 1183 | |
熔体体积流动速率(MVR) | | | |
275°C/5 kg |
25 cm³/10 min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
0.29 % | ISO 294-4 | |
横向(Across Flow) |
0.7 % | ISO 294-4 | |
- |
0.31 % | Internal | constrained |
吸水率 | 7.5 %
| ISO 62 | saturation in water at 23°C |
吸湿率 | 2.24 %
| ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 150 cm³/g
| ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
螺旋流 | 253 mm
| - | Spiral d = 2.0 mm |
氯含量 | 2 ppm
| Internal | Combustion IC |
溴含量 | 1 mg/kg
| Internal | Combustion IC |
碘值 | 1 mg/kg
| Internal | Combustion IC |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
105 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) |
165 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | | | |
断裂(brk) |
10 % | ISO 527-1/-2 | Cond. |
断裂(brk) |
4.3 % | ISO 527-1/-2 | Dry |
弯曲强度 | | | |
- |
150 Mpa | ISO 178 | Cond. |
- |
270 Mpa | ISO 178 | Dry |
弯曲模量 | 5100 Mpa
| ISO 178 | Cond. |
弯曲模量 | 8800 Mpa
| ISO 178 | Dry |
拉伸模量 | 5400 Mpa
| ISO 527-1/-2 | Cond. |
拉伸模量 | 9000 Mpa
| ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
85 kJ/m² | ISO 179/1eA | Cond. |
-30℃ (-22℉) |
8 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) |
18 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) |
12 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
80 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) |
110 kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) |
95 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
220 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
200 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C
| ISO 11357-1/-3 | |
加工温度 | 270~290 °C
| - | injection moulding/extrusion |
模具温度 | 80~90 °C
| - | Injection moulding |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 3.0E+12 Ohm-m
| IEC 62631-3-1 | Dry |
表面电阻率 | 3.0E+15 Ohm
| IEC 62631-3-2 | Cond. |
相比漏电起痕指数(CTI ) | | | |
溶液A |
525 V | IEC 60112 | Cond. |