Ultrasint PA6 X028
PA6
巴斯夫 (BASF)
产品描述
High modulus, high strength and excellent thermal distortion stability are the key features of Ultrasint PA6 X028. These properties ensure precise feature control, very good mechanical properties and simple surface reprocessing of 3D printed parts, in particular for complex shapes or structures. Parts built of this material have similar properties to those of injection molded PA6.
Ultrasint PA6 X028 can fulfill the requirements of functional applications regarding high accuracy and mechanical strength as well as a high heat distortion temperature - properties, where existing 3D printing materials often show limitations.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度热稳定 | |||
| 颜色形状 | 粉末状白色 | |||
| 成型方式 | 激光烧结(SLS)3D打印 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.15 g/cm³ | ISO 1183 | Printed Part |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | 25 cm³/10 min | ISO 1133 | |
粒子大小 | 45 micrometer | Internal | d10 |
粒子大小 | 75 micrometer | Internal | d50 |
粒子大小 | 120 micrometer | Internal | d90 |
堆积(视)密度 | 0.52 g/cm³ | ISO 696 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 78 Mpa | ISO 527-2 | x-direction |
- | 70 Mpa | ISO 527-2 | z-direction |
拉伸延伸率 | |||
断裂(brk) | 13 % | ISO 527-2 | x-direction |
断裂(brk) | 3.2 % | ISO 527-2 | z-direction |
弯曲强度 | |||
- | 121 Mpa | ISO 178 | x-direction |
- | 111 Mpa | ISO 178 | z-direction |
弯曲应变 | |||
断裂(brk) | 6.1 % | ISO 178 | x-direction |
断裂(brk) | 4.1 % | ISO 178 | z-direction |
弯曲模量 | 3300 Mpa | ISO 178 | x-direction |
弯曲模量 | 3300 Mpa | ISO 178 | z-direction |
拉伸模量 | 3550 Mpa | ISO 527-2 | x-direction |
拉伸模量 | 3550 Mpa | ISO 527-2 | z-direction |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 3 kJ/m² | ISO 179 | x-direction |
- | 2.3 kJ/m² | ISO 179 | z-direction |
简支梁无缺口(Charpy Unnotched) | |||
- | 12.6 kJ/m² | ISO 179 | x-direction |
- | 7.4 kJ/m² | ISO 179 | z-direction |
悬臂梁缺口(Izod Notched) | |||
- | 3.1 kJ/m² | ISO 180 | x-direction |
- | 3 kJ/m² | ISO 180 | z-direction |
悬臂梁无缺口(Izod Unnotched) | |||
- | 9.7 kJ/m² | ISO 180 | x-direction |
- | 6.9 kJ/m² | ISO 180 | z-direction |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 190 °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 100 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 199 °C | ISO 306 | 10 N |
维卡软化温度(Vicat) | 201 °C | ISO 306 | 50 N |
线性膨胀系数(CLTE) | |||
- | 135 E-6 mm/mm/℃ | ISO 11359-2 | 90°C |
熔融温度(Tm) | 220 °C | ISO 11357 | 20 K/min |
结晶温度 | 172 °C | ISO 11357 | 20 K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
FMVSS | + pass | FMVSS 302 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 3.1E+13 Ohm-cm | IEC 60093 | |
体积电阻率 | 1.5E+14 Ohm-cm | ISO 3915 | |
表面电阻率 | 1.7E+16 Ohm | IEC 60093 | |
相比漏电起痕指数(CTI ) | |||
- | 575 V | IEC 60112 | 1.20 mm |
绝缘强度 | 27 kV/mm | IEC 60243-1 |