Ultramid® 8202C
PA6
巴斯夫 (BASF)
产品描述
Ultramid 8202C is a modified crystalline and low viscosity, PA6 injection molding homopolymer. It is also available in heat stabilized (Ultramid 8202C HS) and/or pigmented versions. Its unique crystalline structure results in increased strength, stiffness, heat distortion temperature and performance under load as a homopolymer. It also cycles faster while maintaining properties and chemical resistance.
Applications
Ultramid 8202C is ideally suited for applications such as: furniture casters, gears, window hardware, and fittings, insulators, bushings, valves, relays, wiring devices, and other electrical components.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 短周期成型耐化学性低粘度 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
比重 | 1.13 - | ASTM D792 | |
收缩率 | |||
- | 0.9 % | Internal | 3.18 mm |
吸水率 | 1.6 % | ASTM D570 | 24 hr |
吸水率 | 2.6 % | ASTM D570 | 50% RH |
吸水率 | 9.3 % | ASTM D570 | Saturation |
吸水率 | 1.6 % | ISO 62 | 24 hr |
吸水率 | 2.6 % | ISO 62 | 50% RH |
吸水率 | 9.3 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 142 Mpa | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 25 Mpa | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 48 Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 137 Mpa | ASTM D638 | Dry,-40℃ |
屈服(yld) | 30 Mpa | ASTM D638 | Dry,121℃ |
屈服(yld) | 90 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 40 Mpa | ASTM D638 | Dry,80℃ |
屈服(yld) | 142 Mpa | ISO 527 | Conditioned,-40℃ |
屈服(yld) | 25 Mpa | ISO 527 | Conditioned,120℃ |
屈服(yld) | 43 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 30 Mpa | ISO 527 | Conditioned,80℃ |
屈服(yld) | 137 Mpa | ISO 527 | Dry,-40℃ |
屈服(yld) | 30 Mpa | ISO 527 | Dry,120℃ |
屈服(yld) | 25 Mpa | ISO 527 | Dry,150℃ |
屈服(yld) | 88 Mpa | ISO 527 | Dry,23℃ |
屈服(yld) | 40 Mpa | ISO 527 | Dry,80℃ |
断裂(brk) | 80 Mpa | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 20 Mpa | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 70 Mpa | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 30 Mpa | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 130 Mpa | ASTM D638 | Dry,-40℃ |
断裂(brk) | 25 Mpa | ASTM D638 | Dry,121℃ |
断裂(brk) | 90 Mpa | ASTM D638 | Dry,23℃ |
断裂(brk) | 35 Mpa | ASTM D638 | Dry,80℃ |
拉伸延伸率 | |||
屈服(yld) | 3 % | ASTM D638 | Conditioned,-40℃ |
屈服(yld) | 30 % | ASTM D638 | Conditioned,121℃ |
屈服(yld) | 22 % | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 25 % | ASTM D638 | Conditioned,80℃ |
屈服(yld) | 3 % | ASTM D638 | Dry,-40℃ |
屈服(yld) | 27 % | ASTM D638 | Dry,121℃ |
屈服(yld) | 4 % | ASTM D638 | Dry,23℃ |
屈服(yld) | 25 % | ASTM D638 | Dry,80℃ |
屈服(yld) | 22 % | ISO 527 | Conditioned,23℃ |
屈服(yld) | 4 % | ISO 527 | Dry,23℃ |
断裂(brk) | 3 % | ASTM D638 | Conditioned,-40℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,121℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,80℃ |
断裂(brk) | 5 % | ASTM D638 | Dry,-40℃ |
断裂(brk) | 100 % | ASTM D638 | Dry,121℃ |
断裂(brk) | 12 % | ASTM D638 | Dry,23℃ |
断裂(brk) | 100 % | ASTM D638 | Dry,80℃ |
标称断裂伸长率 | 3 % | ISO 527 | Conditioned,-40℃ |
标称断裂伸长率 | 100 % | ISO 527 | Conditioned,120℃ |
标称断裂伸长率 | 50 % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | 100 % | ISO 527 | Conditioned,80℃ |
标称断裂伸长率 | 5 % | ISO 527 | Dry,-40℃ |
标称断裂伸长率 | 100 % | ISO 527 | Dry,120℃ |
标称断裂伸长率 | 7 % | ISO 527 | Dry,23℃ |
标称断裂伸长率 | 100 % | ISO 527 | Dry,80℃ |
弯曲强度 | |||
- | 168 Mpa | ASTM D790 | Conditioned,-40℃ |
- | 42 Mpa | ASTM D790 | Conditioned,23℃ |
- | 183 Mpa | ASTM D790 | Dry,-40℃ |
- | 21 Mpa | ASTM D790 | Dry,121℃ |
- | 110 Mpa | ASTM D790 | Dry,23℃ |
- | 30 Mpa | ASTM D790 | Dry,65℃ |
- | 95 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 4200 Mpa | ASTM D790 | Conditioned,-40℃ |
弯曲模量 | 970 Mpa | ASTM D790 | Conditioned,23℃ |
弯曲模量 | 3370 Mpa | ASTM D790 | Dry,-40℃ |
弯曲模量 | 385 Mpa | ASTM D790 | Dry,121℃ |
弯曲模量 | 3170 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 600 Mpa | ASTM D790 | Dry,65℃ |
弯曲模量 | 440 Mpa | ASTM D790 | Dry,90℃ |
弯曲模量 | 2800 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 1360 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 4090 Mpa | ISO 527 | Dry,-40℃ |
拉伸模量 | 550 Mpa | ISO 527 | Dry,120℃ |
拉伸模量 | 445 Mpa | ISO 527 | Dry,150℃ |
拉伸模量 | 3700 Mpa | ISO 527 | Dry,23℃ |
拉伸模量 | 750 Mpa | ISO 527 | Dry,80℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 3.5 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 21 J/m | ASTM D256 | Conditioned |
-40℃ (-40℉) | 32 J/m | ASTM D256 | Dry |
23℃ (73℉) | 171 J/m | ASTM D256 | Conditioned |
23℃ (73℉) | 48 J/m | ASTM D256 | Dry |
落锤冲击 | 271 J | Internal | Conditioned,23℃ |
落锤冲击 | 122 J | Internal | Dry,23℃ |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 120 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 190 °C | ASTM D648 | Dry |
0.45 Mpa (66 psi)（4.6kg/cm²） | 165 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 75 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 65 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,0.71mm | 65 °C | UL 746B | |
冲击w/impact,1.5/1.6 mm | 75 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 75 °C | UL 746B | |
冲击w/impact,6.0mm | 75 °C | UL 746B | |
电气Elec,0.71mm | 125 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 125 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 125 °C | UL 746B | |
电气Elec,6.0mm | 125 °C | UL 746B | |
强度w/o impact,0.71mm | 65 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 85 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 85 °C | UL 746B | |
强度w/o impact,6.0mm | 85 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 81 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.71 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
V-2 | 6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.5 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry |
绝缘强度 | 30 kV/mm | ASTM D149 | Dry,Short Time, 1.5 mm |