Ultrasint PA6 FR black
PA6
巴斯夫 (BASF)
产品描述
All Ultrasint PA6 grades have in common that they show high modulus, high strength and excellent thermal distortion stability. These properties ensure precise feature control, very good mechanical properties and simple surface reprocessing of 3D printed parts.
Parts made of Ultrasint PA6 FR black reach a V2 rating (UL 94V) and boast of high modulus, high strength and excellent thermal distortion stability, making the material suitable for prototyping and small series production in automotive, transportation, E&E and aerospace applications. Ultrasint PA6 FR black can fulfill the requirements of functional applications regarding high accuracy and mechanical strength as well as a high heat distortion temperature - properties, where existing 3D printing materials often show limitations.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度耐热热稳定阻燃 | |||
| 颜色形状 | 粉末状黑色 | |||
| 成型方式 | 激光烧结(SLS)3D打印 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ISO 1183 | Printed Part |
熔体体积流动速率(MVR) | |||
240℃/2.16 kg | 10 cm³/10 min | ISO 1133 | |
粒子大小 | 65~75 micrometer | Internal | d50 |
堆积(视)密度 | 0.55 g/cm³ | ISO 60 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 41 Mpa | ISO 527-2 | cond,x-direction |
- | 27 Mpa | ISO 527-2 | cond,z-direction |
- | 56 Mpa | ISO 527-2 | dry,x-direction |
- | 33 Mpa | ISO 527-2 | dry,z-direction |
拉伸延伸率 | |||
断裂(brk) | 2.6 % | ISO 527-2 | cond,x-direction |
断裂(brk) | 1.2 % | ISO 527-2 | cond,z-direction |
断裂(brk) | 1.4 % | ISO 527-2 | dry,x-direction |
断裂(brk) | 0.8 % | ISO 527-2 | dry,z-direction |
弯曲强度 | |||
- | 58 Mpa | ISO 178 | cond,x-direction |
- | 40 Mpa | ISO 178 | cond,z-direction |
- | 75 Mpa | ISO 178 | dry,x-direction |
- | 48 Mpa | ISO 178 | dry,z-direction |
弯曲应变 | |||
断裂(brk) | 4.3 % | ISO 178 | cond,x-direction |
断裂(brk) | 2.5 % | ISO 178 | cond,z-direction |
断裂(brk) | 1.8 % | ISO 178 | dry,x-direction |
断裂(brk) | 1.3 % | ISO 178 | dry,z-direction |
弯曲模量 | 2000 Mpa | ISO 178 | cond,x-direction |
弯曲模量 | 2050 Mpa | ISO 178 | cond,z-direction |
弯曲模量 | 4400 Mpa | ISO 178 | dry,x-direction |
弯曲模量 | 3850 Mpa | ISO 178 | dry,z-direction |
拉伸模量 | 2450 Mpa | ISO 527-2 | cond,x-direction |
拉伸模量 | 2450 Mpa | ISO 527-2 | cond,z-direction |
拉伸模量 | 4750 Mpa | ISO 527-2 | dry,x-direction |
拉伸模量 | 4500 Mpa | ISO 527-2 | dry,z-direction |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 1.6 kJ/m² | ISO 179 | cond,x-direction |
- | 1.1 kJ/m² | ISO 179 | cond,z-direction |
- | 1.3 kJ/m² | ISO 179 | dry,x-direction |
- | 1 kJ/m² | ISO 179 | dry,z-direction |
简支梁无缺口(Charpy Unnotched) | |||
- | 7.4 kJ/m² | ISO 179 | cond,x-direction |
- | 3.6 kJ/m² | ISO 179 | cond,z-direction |
- | 4.8 kJ/m² | ISO 179 | dry,x-direction |
- | 2.5 kJ/m² | ISO 179 | dry,z-direction |
悬臂梁缺口(Izod Notched) | |||
- | 2.1 kJ/m² | ISO 180 | cond,x-direction |
- | 1.5 kJ/m² | ISO 180 | cond,z-direction |
- | 1.8 kJ/m² | ISO 180 | dry,x-direction |
- | 1.5 kJ/m² | ISO 180 | dry,z-direction |
悬臂梁无缺口(Izod Unnotched) | |||
- | 7 kJ/m² | ISO 180 | cond,x-direction |
- | 3.8 kJ/m² | ISO 180 | cond,z-direction |
- | 5 kJ/m² | ISO 180 | dry,x-direction |
- | 3.4 kJ/m² | ISO 180 | dry,z-direction |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 207 °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 113 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 214 °C | ISO 306 | 10 N |
维卡软化温度(Vicat) | 197 °C | ISO 306 | 50 N |
熔融温度(Tm) | 218 °C | ISO 11357 | 20 K/min |
结晶温度 | 169 °C | ISO 11357 | 20 K/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.8~3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 750 °C | IEC 60695-2-12 | |
1.6mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 775 °C | IEC 60695-2-13 | |
1.6mm | 775 °C | IEC 60695-2-13 | |
1.8mm | 775 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
热线圈起燃性(HWI) | 4 PLC | UL 746A | 1 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746A | 2-3 mm |