Ultramid® 8350 HS BK102
PA6
巴斯夫 (BASF)
产品描述
Ultramid 8350 HS BK102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility.
Applications
Ultramid 8350 HS BK102 is generally recommended for applications such as automotive vacuum tubing, cable jacketing, and high pressure and hydraulic hoses.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击高韧性 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
比重 | 1.07 - | ASTM D792 | |
收缩率 | |||
- | 1.4 % | Internal | 3.18 mm |
吸水率 | 1.1 % | ASTM D570 | 24 hr |
吸水率 | 1.9 % | ASTM D570 | 50% RH |
吸水率 | 6.7 % | ASTM D570 | Saturation |
吸水率 | 1.1 % | ISO 62 | 24 hr |
吸水率 | 1.9 % | ISO 62 | 50% RH |
吸水率 | 6.7 % | ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 32 Mpa | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 55 Mpa | ASTM D638 | Dry,23℃ |
屈服(yld) | 32 Mpa | ISO 527 | Conditioned,23℃ |
屈服(yld) | 52 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
屈服(yld) | 9 % | ASTM D638 | Conditioned,23℃ |
屈服(yld) | 5 % | ASTM D638 | Dry,23℃ |
屈服(yld) | 9 % | ISO 527 | Conditioned,23℃ |
屈服(yld) | 4.5 % | ISO 527 | Dry,23℃ |
断裂(brk) | 100 % | ASTM D638 | Conditioned,23℃ |
断裂(brk) | 100 % | ASTM D638 | Dry,23℃ |
标称断裂伸长率 | 50 % | ISO 527 | Conditioned,23℃ |
标称断裂伸长率 | 50 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 65 Mpa | ASTM D790 | Dry,23℃ |
- | 55 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 1890 Mpa | ASTM D790 | Dry,23℃ |
弯曲模量 | 1600 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 675 Mpa | ISO 527 | Conditioned,23℃ |
拉伸模量 | 1800 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 83 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 10 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | NB J/m | ASTM D256 | Dry |
23℃ (73℉) | NB kJ/m² | ISO 180 | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 78 R | ASTM D785 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 56 °C | ASTM D648 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 50 °C | ISO 75 | Dry |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 65 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm | 65 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 65 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 65 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm | 65 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm | 65 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 106 E-6 mm/mm/℃ | ASTM D E831 | Dry |
熔融温度(Tm) | 220 °C | ASTM D3418 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | ASTM D257 | Dry,1.5 mm |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | Dry |