Ultramid® B3WGM24 HPX BK23210
Ultramid® B3WGM24 HPX BK23210
PA6
巴斯夫 (BASF)
产品描述
Ultramid B3WGM24 HPX BK23210 is a very high productivity, 30% glass/mineral reinforced heat stabilized injection molding PA6 grade for components that require medium rigidity, excellent dimensional stability, low warpage out of the tool and excellent appearance.
Applications
Typical applications include automobile engine covers, housings and automotive door handles.
基本信息
| 原厂资料 | 物性表-ISO(英文) |
| 产品特性 | 热稳定良好表面尺寸稳定低翘曲短周期成型填充增强 |
| 成型方式 | 注塑 |
| 增强填充 | 30% 玻纤+矿物 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.36 g/cm³
| ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
110 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | | | |
断裂(brk) |
3 % | ISO 527 | Dry,23℃ |
弯曲模量 | 7960 Mpa
| ISO 178 | Dry,23℃ |
拉伸模量 | 7900 Mpa
| ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
4.4 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | | | |
-40℃ (-40℉) |
4.4 kJ/m² | ISO 180 | Dry |
23℃ (73℉) |
5.2 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
210 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） |
190 °C | ISO 75 | Dry |
熔融温度(Tm) | 220 °C
| ISO 3146 | Dry |