Miramid® VEP15C
PA6
巴斯夫 (BASF)
产品描述
Miramid® VEP15C is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for injection molding.
Important attributes of Miramid® VEP15C are:
Flame Rated
Chemical Resistant
Crystalline
Good Stiffness
Impact Modified
Typical applications include:
Automotive
Engineering/Industrial Parts
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性高冲击耐化学性填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | Dry |
吸水率 | 7.7~8.2 % | ISO 62 | Dry |
吸湿率 | 2.4 % | ISO 1110 | Dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 65 Mpa | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 100 Mpa | ISO 527-2 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 13 % | ISO 527-2 | Conditioned,23℃ |
断裂(brk) | 5 % | ISO 527-2 | Dry,23℃ |
弯曲强度 | |||
- | 80 Mpa | ISO 178 | Conditioned,23℃ |
- | 150 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 3800 Mpa | ISO 527-2 | Conditioned,23℃ |
拉伸模量 | 4800 Mpa | ISO 527-2 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 24 kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | 14 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | 80 kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | 70 kJ/m² | ISO 179/1eU | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 140 Mpa | ISO 2039-1 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 200 °C | ISO 75-2 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |
短周期使用温度 | 180 °C | - | Dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | Dry |
灼热丝可燃性指数(GWFI) | |||
1mm | 650 °C | IEC 60695-2-12 | Dry |
FMVSS | + pass | FMVSS 302 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-cm | IEC 60093 | Conditioned |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | Dry |
相比漏电起痕指数(CTI ) | |||
- | 550 V | IEC 60112 | Dry |