Ultramid® B3WG10 BK00564
PA6
巴斯夫 (BASF)
产品描述
This resin is a heat stabilized, 50% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black weather resistant and pigmented versions.
Applications
Ultramid B3WG10 BK00564 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高强度高刚性耐热尺寸稳定填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.56 g/cm³ | ISO 1183 | |
吸水率 | 1.4 % | ISO 62 | Equilibrium, 23°C, 50% RH |
吸水率 | 4.8 % | ISO 62 | Saturation, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 225 Mpa | ISO 527 | Dry,23℃ |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527 | Dry,23℃ |
弯曲强度 | |||
- | 345 Mpa | ISO 178 | Dry,23℃ |
弯曲模量 | 14500 Mpa | ISO 178 | Dry,23℃ |
拉伸模量 | 16700 Mpa | ISO 527 | Dry,23℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179 | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 90 kJ/m² | ISO 179 | Dry |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 12 kJ/m² | ISO 180 | Dry |
23℃ (73℉) | 15 kJ/m² | ISO 180 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 220 °C | ISO 75 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | 215 °C | ISO 75 | Dry |
熔融温度(Tm) | 220 °C | ISO 3146 | Dry |